Convective polymer assembly for the deposition of nanostructures and polymer thin films on immobilized particles†
Received
31st July 2014
, Accepted 22nd September 2014
First published on 2nd October 2014
Abstract
We report the preparation of polymer particles via convective polymer assembly (CPA). Convection is used to move polymer solutions and cargo through an agarose gel that contains immobilized template particles. This method both coats and washes the particles in a process that is amenable to automation, and does not depend on passive diffusion or electrical currents, thus facilitating incorporation of fragile and nanoscale objects, such as liposomes and gold nanoparticles, into the thin polymer films. Template dissolution leads to the formation of stable polymer particles and capsules.
Introduction
Layer-by-layer (LbL) assembly has been widely used for the engineering of polymer capsules.1–3 Recently, we reported a new paradigm for producing LbL assembled polymer capsules from immobilized template particles.4,5 By immobilizing template particles in a porous hydrogel, namely agarose, polymer solutions can be moved through the hydrogel to coat the immobilized particles. The hydrogel can then be dissolved, allowing for recovery of the layered particles, and after template dissolution, robust nano- and micro-capsules can be formed. Thus far, electrophoretic4 and immersive5 polymer assembly (EPA and IPA, respectively) have been used to coat particles in a rapid or automated fashion, respectively, with various polymer combinations (electrostatically associated synthetic and biopolymers, and hydrogen bonding polymers) and on template particles of different diameters (from approximately 40 nm to 5 μm). Both EPA and IPA have unique advantages and approach the comprehensive versatility of conventional LbL assembly, which uses centrifugation and washing to separate unbound polymer from the coated template particles. For example, conventional LbL assembly can use different interactions2,6,7 (such as electrostatic,1,8 hydrogen bonding,9,10 or even host guest11–13) and different template particles (such as melamine formaldehyde,1 polystyrene,1 silica,14 gold,15 and calcium carbonate16 of different sizes) for layer build-up. Although choice over templates and polymers provides a broad tool-kit for assembling capsules with different properties, part of the reason LbL capsules have found use in a broad range of fields ranging from biosensing and bioreactions, to drug and vaccine delivery2,6 is their capacity to load and release functional units, or “cargo”.
For polymer capsules, cargo can be loaded and encapsulated before, during, or after capsule preparation.17 Pre-loading can be accomplished by co-precipitating cargo during template formation, or by using templates that can adsorb cargo prior to coating.14,16 In contrast, post-loading can be achieved by making the already prepared capsules permeable and resealing the shell after encapsulation.18 This can be accomplished by changing the salt concentration,19 solvent,20 pH,21–24 and temperature,25 or by cross-linking the capsules.26 Pre- and post-loading exploit the properties of the template and shell compositions, respectively. Loading during assembly is interesting to explore for next generation film assembly techniques because unique cargo can be loaded, such as sensitive materials that may not be stable during the treatments necessary for pre- or post-loading. For example, liposomes27–29 and polymersomes30 have been incorporated during layer build-up to allow for the specific encapsulation and protection of biological cargo. Loading sensitive amphiphilic cargo adds an additional benefit, as the hydrophobic compartments of the structures can be further utilized to load hydrophobic molecules.31 Therefore, it is important to expand the capacity of layering on immobilized template particles to specifically allow for cargo loading during the assembly process, so that large and/or sensitive cargo can be incorporated into the resultant polymer capsules.
Herein, we deposit polymers and cargo on immobilized particles by using convective polymer assembly (CPA), or polymer assembly using a directional flow (Fig. 1). CPA allows for a high-performance liquid chromatography (HPLC) like set-up, using syringe pumps and standard tubing (Fig. S1†), to move the polymer, cargo, and washing solutions past the immobilized template particles, thereby depositing the polymer or cargo on the templates and subsequently removing the unbound polymer. CPA was chosen as the random diffusion associated with IPA would prevent large cargo32 from diffusing through the agarose to achieve deposition on immobilized templates within a reasonable time scale. Similarly, the electric current used in EPA could destabilize sensitive cargo such as liposomes.33,34 Additionally, the template choice for CPA was expanded by using calcined calcium carbonate (CaCO3) particles to form replica particles. Hence, CPA complements IPA and EPA by: (i) allowing deposition of larger cargo by not relying on diffusion; (ii) allowing deposition of sensitive cargo, as no electric current is needed; and (iii) allowing the use of a wider range of templates, as convection does not limit the types of buffers that can be used in the same way as an electrical system, such as EPA, does. CPA therefore addresses some of the challenges associated with IPA and EPA, while retaining advantages such as ease-of-use and high amenability to automation.
![image file: c4nr04348k-f1.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f1.gif) |
| Fig. 1 Schematic illustration of CPA showing polymer flowing into the agarose containing immobilized particles and layer build-up. The resultant LbL core–shell particles can be recovered from the agarose, and the templates can be removed to yield LbL capsules. The polymer flow-through was collected and quantified over four PAH/PSS cycles. Magnified portions of the first bilayer can be seen in Fig. S2.† | |
Experimental details
Preparation of agarose containing particle templates
1%, 2%, and 4% ultra-low gelling agarose gels were prepared in ultrapure water. 150 μL of 50 mg mL−1 silica particles (1.11 or 4.99 μm in diameter) or 150 μL of 10 mg mL−1 calcined CaCO3 particles were added for each 1.5 mL of liquid gel solution. This liquid agarose particle solution was then pipetted into 3DKUBEs (Kiyatec, Greenville, SC, USA).
Convective polymer assembly (CPA)
The 3DKUBE was attached to a 6-way valve and syringe pump (Fig. S1†). The syringe was loaded with ultrapure water and the pump flow rate was set to 100 μL min−1. Poly(allylamine hydrochloride) (PAH, ∼15 kDa) or poly(styrene sulfonate) (PSS, ∼15 kDa), in 0.5 M sodium chloride (NaCl) at pH 7, with a polymer concentration of 0.1 mg mL−1, was loaded into the loading tube and the 6-way valve was switched from “load” to “inject.” 2 mL of polymer solution was loaded through the loading tube to ensure that the polymer remained at the required concentration and was not diluted. The process was repeated for each polymer layer until the desired number of layers was achieved. Polymer was injected every 75 min for the initial characterization of the flow-through, and every 45 min for all subsequent layering experiments.
Cargo loading
The gold nanoparticles (Au NPs; ∼15 nm in diameter) or liposomes (∼100 nm in diameter) were loaded similarly to PAH and PSS, except for the buffers used. The Au NPs were dispersed in ultrapure water and the liposomes were dispersed in HEPES buffer (10 mM HEPES, 150 mM NaCl, pH 7.4). The Au NPs were loaded after 3.5 bilayers of PAH/PSS and the liposomes were loaded after 4 bilayers of PAH/PSS, and both were finally capped with one bilayer of PAH/PSS.
Sample recovery
The agarose containing layered particles was removed from the 3DKUBE and placed into a microcentrifuge tube. Ultrapure water was added to the tube, which was heated (45 °C) until the agarose dissolved. The melted solution was centrifuged at 37 °C at 800 g for 30 s to pellet the particles. The supernatant was removed and discarded. The particles were washed six times to remove the excess agarose and finally resuspended in ultrapure water.
Core removal
300 μL of hydrofluoric acid (5 M HF) or 40 mM sodium acetate, pH 4 was added to the layered particles, and incubated for 5 min to remove the silica or CaCO3, respectively. [Caution! HF is highly toxic. Extreme care should be taken when handling HF solution.] The capsules or replica particles were pelleted at 2700 g for 3 min, the supernatant was removed and they were then washed with ultrapure water three times to ensure that the HF or sodium acetate was fully removed.
Additional experimental details can be found in the ESI.†
Results and discussion
Firstly, we investigated the behavior of the agarose containing silica particles, and the movement of polymers through the agarose under convection. Note that columns could also be used with the primary driving forces being gravity and the capillary effect (data not shown), but our analysis hereafter is focused on the HPLC-like set-up (Fig. S1†). We observed that when using a flow rate of 100 μL min−1, 1% and 2% ultra-low gelling agarose gels would liquefy and flow out of the 3DKUBE during CPA, and we therefore restricted our analysis to 4% gels. The modular set-up and constant flow rate let us investigate the movement of polymer into and out of the agarose by analyzing fractions of the flow-through (Fig. 1 and S2†). The UV-Vis absorbance of the flow-through was used to quantify the amount of polymer adsorbed onto the immobilized particles. An average of ∼10 μg of PAH and ∼10 μg of PSS was deposited for each bilayer. Similar values from literature (i.e., 8–16 μg for PAH and 9–12 μg for PSS) are attained when values are normalized to the approximate surface area of the particles (∼19 cm2).1,35,36 This suggests that CPA provides a similar coating coverage to conventional (i.e., non-flow adsorption/centrifugation/wash) LbL assembly. The polymer reached its peak in the flow-through roughly 10 min after injection, which corresponds to 1 mL of polymer solution. This is the same volume as the agarose, suggesting that the polymer solution was flowing through the agarose matrix. The polymer solution reached background levels, corresponding to less than 0.1 μg of PAH and less than 0.4 μg of PSS, 30–45 min after injection. This equates to 3 to 4 mL of washing volume, which is comparable to the washing procedure for conventional centrifugation/wash LbL assembly (3 to 4 wash cycles). Characterization of the flow-through demonstrated that the process could be sped up by injecting the polymer solutions 45 min after one another, and indicates that even shorter times should be possible with higher flow rates. This injection time (45 min) was used for all subsequent experiments.
By removing and sectioning the agarose prior to washing, it was observed that the concentration of polymer reduced around the template particles from as far away as ∼2 μm (Fig. S3†). Polymer build-up on the immobilized template particles during CPA was characterized using fluorescently labeled PAH. Flow cytometry showed a linear fluorescence growth for polymer build-up, and after four bilayers, capsules were obtained (Fig. 2a). Height analysis using atomic force microscopy (AFM) revealed a bilayer thickness of ∼2.5 nm (Fig. 2b), which corresponds well with the literature value for four bilayer PAH/PSS capsules.37 Interestingly, this is an intermediary value compared to films formed with EPA and IPA, which both also use immobilized template particles. EPA yields roughly twice the thickness (∼5 nm) for each bilayer,4 while IPA gives half (∼1.25 nm) for each bilayer.5 Together with the flow-through analysis, the height measurements demonstrate that CPA is comparable to conventional polymer assembly techniques. Energy-dispersive X-ray (EDX) mapping was also used to confirm the presence of elements unique to each polymer (Fig. 2c and d). The capsules contained nitrogen from PAH and sulfur from PSS, demonstrating that both polymers were present.
![image file: c4nr04348k-f2.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f2.gif) |
| Fig. 2 Layer build-up and characterization of four bilayer PAH/PSS capsules. (a) Fluorescence intensity was measured for core–shell particles after the deposition of each bilayer. (Inset) Fluorescently labeled capsules prepared via CPA using PAH-FITC. (b) AFM image and height profile of a capsule. EDX mapping of a capsule for (c) sulfur and (d) nitrogen. The scale bars are (a) 10 μm, and (c) and (d) 1 μm. | |
The constant flow of water associated with CPA was then used for the deposition of larger objects into the polymer films. This is possible due to the relatively large pore-size associated with agarose (∼50 nm to 10 μm)5 and that the flow in CPA is unidirectional. Au NPs (Fig. 3a) were loaded as a proof of concept. Au NPs have previously been incorporated in capsules to allow for photo-induced therapeutic release.38 The Au NP-loaded capsules were robust and stable in water, as observed by fluorescence microscopy (Fig. 3b). The Au NPs were detected with EDX (Fig. S4†) and more accurately, EDX mapping was used to confirm that the gold was present in the capsules (Fig. 3c). By weight, the gold to sulfur ratio was 1
:
399, indicating that ∼25 ng of Au NPs was deposited, corresponding to approximately 70 Au NPs per capsule. The Au NPs present in the capsule wall were also imaged with TEM (Fig. 3d). The loading of Au NPs demonstrated the capacity of CPA to move and load solid structures larger than standard polymers.
![image file: c4nr04348k-f3.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f3.gif) |
| Fig. 3 PAH/PSS capsules loaded with Au NPs via CPA. (a) TEM image of Au NPs. (b) Fluorescence microscopy image of the Au NP-loaded capsules. PAH-FITC was used as the fluorescent polymer. (c) High angle annular dark-field (HAADF) image of a capsule, inset with EDX mapping for gold. (d) TEM image of the same capsule in (c) with Au NPs visible. The scale bars are (a) 20 nm, (b) 10 μm, and (c) and (d) 200 nm. | |
Next, liposomes were loaded into the capsule shell to test the loading of more fragile cargo. Loading was detected through fluorescence microscopy and indirectly through the loading of hydrophobic cargo into the liposomes. The liposomes were labelled with a fluorescent phospholipid during formation,27 and consequently the fluorescence was visible in the capsule shell (Fig. 4).
![image file: c4nr04348k-f4.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f4.gif) |
| Fig. 4 PAH/PSS capsules loaded with fluorescently labelled liposomes via CPA. Images of capsules acquired using (a) differential interference contrast (DIC) microscopy, and (b) fluorescence microscopy. The scale bars are 5 μm. | |
Additionally, a hydrophobic dye (naphthofluorescein) was loaded into the liposomes of both core–shell particles (Fig. 5) and capsules (Fig. S5†), confirming the presence of the liposomes. The fluorescence of the dye became concentrated around the core–shell particles due to the dye migrating into the liposomes, which also greatly reduced the fluorescence intensity of the solution. Similar results were seen for the capsules (Fig. S5 and S6†). For both core–shell particles and capsules, the addition of Triton-X-100 disrupted the liposomal structures and allowed the dye to escape back into the solution. The loading of both the Au NPs and the liposomes demonstrated that larger cargo can be successfully incorporated into the capsules prepared from immobilized template particles using CPA.
![image file: c4nr04348k-f5.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f5.gif) |
| Fig. 5 Loading of PAH/PSS-liposome core–shell particles with a hydrophobic dye, naphthofluorescein. Fluorescence microscopy images of PAH/PSS-liposome core–shell particles with the corresponding DIC images in the insets: (a) before and (b) after Triton X-100 treatment. (c) Control, liposome-free PAH/PSS core–shell particles after the addition of naphthofluorescein. The scale bars are 5 μm. | |
Finally, to demonstrate the versatility of CPA being applicable to other template particles, mesoporous calcined CaCO3 particles were used (Fig. 6a and S7†). CaCO3 particles are of particular interest for CPA as the acetate buffers used in EPA readily degrades CaCO3.4 Using CPA, 4 bilayers of PAH/PSS were deposited on the CaCO3 particles, after which the CaCO3 core was removed using acetate buffers. The resulting polymer replica particles resembled particles more so than capsules (Fig. 6b). The use of CaCO3 particles as templates greatly extends the application of CPA because the formation of CaCO3 particles can be performed in the presence of therapeutics, which would allow CPA capsules and particles to be pre-loaded.
![image file: c4nr04348k-f6.tif](/image/article/2014/NR/c4nr04348k/c4nr04348k-f6.gif) |
| Fig. 6 Polymer replica particles prepared from calcined CaCO3 template particles via CPA. (a) DIC image of the calcined CaCO3 template particles. (b) PAH/PSS replica particles after template removal, produced via CPA. The scale bars are 10 μm. | |
Conclusions
This study highlights the use of an immobilizing matrix as an appropriate paradigm from which polymer assembly and cargo loading can be performed for the preparation of engineered particles. We have demonstrated the use of a directional flow for depositing polymers, nanoparticles, and liposomes onto immobilized template particles for the formation of microcapsules and polymer replica particles. Convection allows for the layering of larger materials (such as Au NPs and liposomes) that would not passively diffuse through the agarose matrix on a reasonable timescale. The shell thickness of the capsules prepared via CPA falls in between the thicknesses for capsules prepared via EPA and IPA, and is similar to those prepared by conventional (i.e., adsorption/centrifugation/wash) LbL assembly.37 Additionally, porous template particles, namely CaCO3, were used for the formation of polymer replica particles. This technique has the potential to be incorporated into macro- and microfluidic systems,39 thereby greatly expanding the variety of equipment and approaches applicable towards the coating of particulate templates. This includes the use of commercially available computer-controlled automatic systems for loading and injection, commonly used in HPLC-setups, which could allow an arbitrary number of layers to be programmed and then performed through repeated automatic loading/injection cycles requiring little to no hands-on time. This would also allow for automation and high-throughput studies to be conducted in parallel. Similarly, higher flow rates and reaction chambers of different dimensions could be used to speed up the layering and washing times. Furthermore, CPA could be combined with EPA4 and IPA5 to allow for the benefits of each technique to be used when necessary. For example, thick polymer layers could be deposited using EPA, CPA could be used to add cargo, and finally IPA could be used to autonomously coat different batches at the same time.
Acknowledgements
This work was supported by the Australian Research Council (ARC) under the Australian Laureate Fellowship (F.C., FL120100030) and the Super Science Fellowship (F.C., FS110200025) schemes as well as the Australian Government through an Australian Postgraduate Award (M.B.) and an International Postgraduate Research Scholarship (M.B.). This research was also conducted and funded by the ARC Centre of Excellence in Convergent Bio-Nano Science and Technology (project number CE140100036).
Notes and references
- F. Caruso, R. A. Caruso and H. Möhwald, Science, 1998, 282, 1111–1114 CrossRef CAS.
- S. De Koker, R. Hoogenboom and B. G. De Geest, Chem. Soc. Rev., 2012, 41, 2867–2884 RSC.
- Y. Yan, M. Björnmalm and F. Caruso, Chem. Mater., 2014, 26, 452–460 CrossRef CAS.
- J. J. Richardson, H. Ejima, S. L. Lörcher, K. Liang, P. Senn, J. Cui and F. Caruso, Angew. Chem., Int. Ed., 2013, 52, 6455–6458 CrossRef CAS PubMed.
- J. J. Richardson, K. Liang, K. Kempe, H. Ejima, J. Cui and F. Caruso, Adv. Mater., 2013, 25, 6874–6878 CrossRef CAS PubMed.
- C. S. Peyratout and L. Dahne, Angew. Chem., Int. Ed., 2004, 43, 3762–3783 CrossRef CAS PubMed.
- K. Ariga, J. P. Hill and Q. Ji, Phys. Chem. Chem. Phys., 2007, 9, 2319–2349 RSC.
- E. Donath, G. B. Sukhorukov, F. Caruso, S. A. Davis and H. Möhwald, Angew. Chem., Int. Ed., 1998, 37, 2201–2205 CrossRef.
- Y. Zhang, S. Yang, Y. Guan, W. Cao and J. Xu, Macromolecules, 2003, 36, 4238–4240 CrossRef CAS.
- V. Kozlovskaya, S. Ok, A. Sousa, M. Libera and S. A. Sukhishvili, Macromolecules, 2003, 36, 8590–8592 CrossRef CAS.
- Z. Wang, Z. Feng and C. Gao, Chem. Mater., 2008, 20, 4194–4199 CrossRef CAS.
- G. V. Dubacheva, P. Dumy, R. Auzély, P. Schaaf, F. Boulmedais, L. Jierry, L. Coche-Guerente and P. Labbé, Soft Matter, 2010, 6, 3747–3750 RSC.
- O. Crespo-Biel, B. Dordi, D. N. Reinhoudt and J. Huskens, J. Am. Chem. Soc., 2005, 127, 7594–7600 CrossRef CAS PubMed.
- Y. Wang, A. Yu and F. Caruso, Angew. Chem., Int. Ed., 2005, 117, 2948–2952 CrossRef.
- D. C. Zhiyong Poon, X. Zhao and P. T. Hammond, ACS Nano, 2011, 5, 4284–4292 CrossRef PubMed.
- G. B. Sukhorukov, D. V. Volodkin, A. M. Günther, A. I. Petrov, D. B. Shenoy and H. Möhwald, J. Mater. Chem., 2004, 14, 2073–2081 RSC.
- B. G. De Geest, N. N. Sanders, G. B. Sukhorukov, J. Demeester and S. C. De Smedt, Chem. Soc. Rev., 2007, 36, 636–649 RSC.
- E. Kharlampieva, V. Kozlovskaya and S. A. Sukhishvili, Adv. Mater., 2009, 21, 3053–3065 CrossRef CAS.
- A. A. Antipov, G. B. Sukhorukov, S. Leporatti, I. L. Radtchenko, E. Donath and H. Möhwald, Colloids Surf., A, 2002, 198, 535–541 CrossRef.
- Y. Lvov, A. A. Antipov, A. Mamedov, H. Möhwald and G. B. Sukhorukov, Nano Lett., 2001, 1, 125–128 CrossRef CAS.
- G. B. Sukhorukov, A. A. Antipov, A. Voigt, E. Donath and H. Möhwald, Macromol. Rapid Commun., 2001, 22, 44–46 CrossRef CAS.
- S. Y. Yang, D. Lee, R. E. Cohen and M. F. Rubner, Langmuir, 2004, 20, 5978–5981 CrossRef CAS.
- E. Kharlampieva and S. A. Sukhishvili, Langmuir, 2004, 20, 9677–9685 CrossRef CAS PubMed.
- N. G. Balabushevich, O. P. Tiourina, D. V. Volodkin, N. I. Larionova and G. B. Sukhorukov, Biomacromolecules, 2003, 4, 1191–1197 CrossRef CAS PubMed.
- J. F. Quinn and F. Caruso, Langmuir, 2004, 20, 20–22 CrossRef CAS.
- H. Zhu and M. J. McShane, Langmuir, 2005, 21, 424–430 CrossRef CAS PubMed.
- B. Städler, A. D. Price, R. Chandrawati, L. Hosta-Rigau, A. N. Zelikin and F. Caruso, Nanoscale, 2009, 1, 68–73 RSC.
- B. Städler, R. Chandrawati, A. D. Price, S.-F. Chong, K. Breheney, A. Postma, L. A. Connal, A. N. Zelikin and F. Caruso, Angew. Chem., Int. Ed., 2009, 48, 4359–4362 CrossRef PubMed.
- R. Chandrawati, P. D. Odermatt, S.-F. Chong, A. D. Price, B. Städler and F. Caruso, Nano Lett., 2011, 11, 4958–4963 CrossRef CAS PubMed.
- H. Lomas, A. P. R. Johnston, G. K. Such, Z. Zhu, K. Liang, M. P. van Koeverden, S. Alongkornchotikul and F. Caruso, Small, 2011, 7, 2109–2119 CrossRef CAS PubMed.
- L. Hosta-Rigau, B. Städler, Y. Yan, E. C. Nice, J. K. Heath, F. Albericio and F. Caruso, Adv. Funct. Mater., 2010, 20, 59–66 CrossRef CAS.
- A. Pluen, P. A. Netti, R. K. Jain and D. A. Berk, Biophys. J., 1999, 77, 542–552 CrossRef CAS.
- D. Dimitrov and M. Angelova, J. Electroanal. Chem., 1988, 253, 323–336 CrossRef.
- P. S. O'Shea, G. Petrone, R. Casey and A. Azzi, Biochem. J., 1984, 219, 719–726 Search PubMed.
- Z. Feldötö, I. Varga and E. Blomberg, Langmuir, 2010, 26, 17048–17057 CrossRef PubMed.
- Y. Lvov, K. Ariga, M. Onda, I. Ichinose and T. Kunitake, Colloids Surf., A, 1999, 146, 337–346 CrossRef CAS.
- S. Leporatti, A. Voigt, R. Mitlohner, G. Sukhorukov, E. Donath and H. Möhwald, Langmuir, 2000, 16, 4059–4063 CrossRef CAS.
- A. S. Angelatos, B. Radt and F. Caruso, J. Phys. Chem. B, 2005, 109, 3071–3076 CrossRef CAS PubMed.
- M. Björnmalm, Y. Yan and F. Caruso, J. Controlled Release, 2014, 190, 139–149 CrossRef PubMed.
Footnotes |
† Electronic supplementary information (ESI) available: Detailed experimental/instrumental information and supporting figures. See DOI: 10.1039/c4nr04348k |
‡ Present address: CSIRO Process Science and Engineering, Clayton, Victoria 3168, Australia |
§ Present address: Graduate School of Chemical Sciences and Engineering, Hokkaido University, Sapporo, Japan |
¶ Present address: Institute of Industrial Science, The University of Tokyo, Tokyo, Japan |
|
This journal is © The Royal Society of Chemistry 2014 |