Mingzhao Liu and Philippe Guyot-Sionnest*
James Franck Institute, The Ellen and Melvin Gordon Center for Integrative Science, The University of Chicago, 929 East 57th Street, Chicago, Illinois 60637, USA. E-mail: pgs@uchicago.edu; Tel: +1 773 703 3463
First published on 20th July 2006
A homogeneous layer of silver sulfide or selenide was coated onto gold nanorods in aqueous solution by exposing Au/Ag core/shell nanorods to S2− or Se2− in an oxidizing environment. The formation of the silver chalcogenide layers was confirmed by transmission electron microscopy (TEM) and selective area electron diffraction (SAED). The longitudinal plasmon resonance of the gold nanorods shifted to the red and was attenuated. The experimental spectra agree well with a simulation based on confocal ellipsoids in the quasi-static limit. The synthetic procedure was also employed to coat silver sulfide or selenide onto gold bipyramids. A red-shift of the longitudinal plasmon resonance was also seen, although the coating was not as homogeneous. These novel composite materials may present interesting nonlinear optical properties.
Recently, there has been significant interest in hybrid nanostructures with tunable optical properties.6,7 Some functionalized plasmonic systems, with magnetic (magnetite-Au) or exitonic properties (PbSe-Au), have also been reported.8 In this paper, we report a procedure to coat a thin layer of silver sulfide or silver selenide of controllable thickness over gold nanorods.
In order to convert the silver layer to silver sulfide, an excess of 10 mM freshly prepared sodium sulfide aqueous solution was mixed with the Au/Ag core/shell nanorods. The colour of the solution changed from green to pink upon mixing. The mixture was stirred in a vessel open to air for a few hours towards the end of the reaction. The final solution was more or less brownish, depending on the thickness of the starting silver layer. It is important for the solution to be in contact with air, as seen in the balanced reaction:
4 Ag + 2 S2− + O2 + 2 H2O → 2 Ag2S + 4 OH− |
To make a silver selenide layer instead, the sodium sulfide solution was replaced by selenourea ((NH2)2CSe). Selenourea is quickly hydrolyzed and releases free Se2−in situ. A similar reaction as above then leads to the formation of silver selenide. The solution of the silver selenide coated gold nanorods is dark brownish.
The formation and the uniformity of the silver chalcogenides layers were checked with the Transmission Electron Microscope (TEM). The gold nanorods shown here have diameter 14.0 ± 2.9 nm and aspect ratio 3.3 ± 0.7. The statistics were obtained by measuring about 100 gold nanorods from the TEM images. As seen in Fig. 1(b), a layer of ∼2 nm thickness attributed to silver was coated onto the surface of the gold nanorods. After the conversion to sulfide or selenide, its thickness became ∼3.5 nm, leaving the gold core unchanged (Fig. 1(c), (d)). The thickness of the silver sulfide or selenide layer is controlled by the thickness of the silver layer, i.e., a thinner silver layer gives a thinner silver chalcogenide layer.
![]() | ||
Fig. 1 TEM images of (a) gold nanorods, (b) Au/Ag core/shell nanorods, (c) Au/Ag2S core/shell nanorods, and (d) Au/Ag2Se core/shell nanorods. Scale bars = 50 nm. |
In order to confirm the formation of the silver chalcogenide layers, we performed selective area electron diffraction (SAED) measurements on the samples (Fig. 2). The measured d values were then compared with the JCPDS (Joint Committee for Powder Diffraction Studies) cards. For the Au/Ag2S core/shell nanorods, the diffraction pattern is found to be consistent with monoclinic Ag2S (acanthite, PDF (Powder Diffraction File) card 75-1061), which is the low temperature phase (T < 450 K).15 For the Au/Ag2Se core/shell nanorods, the diffraction pattern is found to be consistent with orthorhombic Ag2Se (naumannite, PDF card 71–2410), which is also the low temperature phase (T < 400 K).7
![]() | ||
Fig. 2 The SAED patterns from (left) Au/Ag2S core/shell nanorods, and (right) Au/Ag2Se core/shell nanorods. For each diffraction pattern, there are about 10 particles in the viewing area. Each arrow points to a characteristic spot in the diffraction ring. The diffractions from gold serve as the internal standard, with its lattice constant taken as 4.0786 Å.16 |
The UV-Vis-NIR spectra of the samples were taken to address the effect of the coating and they are shown in Fig. 3. The bare gold nanorods sample has the longitudinal plasmon resonance at 1.68 eV. The resonance is blue-shifted to 1.78 eV upon coating with 2 nm of silver.11 The intensity of the resonance is significantly enhanced, since more free electrons are involved into the plasmon. Once the silver layer is converted to silver chalcogenide, a red-shift of the longitudinal plasmon resonance is seen. The peak is shifted to 1.35 eV for the silver sulfide coating and to 1.28 eV for the silver selenide coating. A smaller red-shift is seen for thinner chalcogenide coatings. The final peak position also depends on the aspect ratio of the gold core. For gold nanorods with the plasmon resonance at 1.45 eV, a 3 nm silver selenide coating shifts the resonance to 1.1 eV. We note that the longitudinal plasmon resonance is attenuated as the silver layer is converted to silver sulfide or silver selenide. This can be explained by the high refractive indices of the silver chalcogenides, which screen the incident electromagnetic field.
![]() | ||
Fig. 3 UV-Vis-NIR spectra of gold nanorods (solid black), Au/Ag core/shell nanorods (solid gray), Au/Ag2S core/shell nanorods (dashed black), and Au/Ag2Se core/shell nanorods (dashed gray). The absorbance values were normalized by the relative concentrations of each solution. |
The procedure described above should be applicable to other gold nanostructures. We tested it on gold bipyramids of ∼25 nm diameter and ∼80 nm length (Fig. 4(a)).10 Although a quite homogeneous silver layer can be coated onto gold nanorod surfaces, this is not the case for coating onto gold bipyramids. Instead, the coating is thicker on the facets, and much thinner around the corners, with almost no silver covering the tip at all (Fig. 4(b)). This coating eventually turns the overall shape of the nanoparticle from bipyramidal to ellipsoidal. We believe that silver preferentially coats the side facets of the bipyramids because of their highly-stepped structure.10 This allows the silver ions to be adsorbed and reduced on them preferably. Once the silver layer is converted to silver sulfide, the thickness profile is preserved, or even magnified (Fig. 4(c)). In contrast, the silver selenide layer appears to be quite even across the surface (Fig. 4(d)), implying that its formation might not be simply due to the diffusion of selenium atoms into the silver lattice.
![]() | ||
Fig. 4 TEM images of (a) gold bipyramids, (b) with silver coating, (c) with silver sulfide coating, and (d) with silver selenide coating. Scale bars = 50 nm. |
The spectrum of the gold bipyramids is changed by the silver layer or the silver chalcogenide layer in a similar way as for the gold nanorods (Fig. 5). The pure Au sample has a very narrow longitudinal plasmon resonance at 1.56 eV, with a 0.12 eV linewidth. This is much narrower than that of the gold nanorods because of the excellent shape-monodispersivity of the gold bipyramids. The spectrum also shows pronounced extinction at 2–2.5 eV. While the extinction partly belongs to the transverse mode of the bipyramids, it is also due to the significant amount of spherical particles in the sample. The silver coating blue-shifts the longitudinal plasmon resonance to 1.76 eV, and broadens the peak to 0.14 eV, because of the extra dispersity on the shape, i.e., the thickness of the silver layer. Once the silver layer is converted to silver chalcogenides, the longitudinal plasmon resonance is red-shifted to 1.1–1.2 eV, and strongly attenuated.
![]() | ||
Fig. 5 UV-Vis-NIR spectra of gold bipyramids (solid black), with silver coating (solid gray), with silver sulfide coating (dashed black), and with silver selenide coating (dashed gray). |
![]() | (1) |
![]() | (2) |
![]() | (3) |
The simulation was made by averaging spectra from a Gaussian distribution of gold core aspect ratios, in order to address the inhomogeneous line-broadening in the experimental data. Bulk dielectric functions were used for the simulation.17 No simulation of silver selenide coated nanorods is provided, since the dielectric function reported for silver selenide does not cover the NIR range. For bare gold nanorods, the diameter is fixed at 14 nm, and a Gaussian distribution at 3.3 ± 0.7 is set for the aspect ratio, according to the measurement from the TEM images. The thicknesses of silver and silver sulfide layers at the equator are fixed at 2 nm and 3.5 nm, respectively. The simulation results for bare gold nanorods (Fig. 6) closely resemble the experimental spectrum in Fig. 3. For the silver coated ones, the longitudinal plasmon is enhanced and blue-shifted, in agreement with the experimental results. However, a smaller blue-shift is seen in the experimental spectrum. The reason is possibly that the thin layer (2 nm) of silver has a different dielectric constant than Ag bulk, as a result of the increased surface scattering of free electrons.11,18 For silver sulfide coated nanorods, the experimental data and simulation agree well within the whole spectral range. The longitudinal plasmon resonance is red-shifted by 0.3 eV and gets attenuated, although more attenuation is seen in the experimental result possibly because there is also a distribution of thicknesses of the silver sulfide layer, which is neglected in the simulation. The increasing extinction of Au/Ag2S core/shell nanorods in the UV range, which is a result of the increasing absorption by silver sulfide, is also nicely reproduced by the simulation.
![]() | ||
Fig. 6 Simulated extinction spectra of gold nanorods (solid black), Au/Ag core/shell nanorods (solid gray), and Au/Ag2S core/shell nanorods (dashed black) immersed in a medium with εm = 1.77.19 |
Footnote |
† This paper is part of a Journal of Materials Chemistry theme issue on Anisotropic Nanomaterials. Guest editor: Luis Liz-Marzan. |