Micelles and gels of oxyethylene–oxybutylene diblock copolymers in aqueous solution: The effect of oxyethylene-block length

Abstract

Block copolymer E₉₀B₁₀ (E=oxyethylene, B=oxybutylene) was synthesised and characterised by gel permeation chromatography and ¹³C NMR spectroscopy. Dynamic light scattering (DLS) and static light scattering (SLS) were used to characterise the micelles in solution (both in water and in aqueous 0.2 mol dm^-3 K₂SO₄), yielding the micellar association numbers, the hydrodynamic and thermodynamic radii, and related expansion factors. Micellar parameters were also obtained by small-angle neutron scattering (SANS) for solutions of a similar copolymer, E₈₆B₁₀, in water, i.e., the association number, the hard-sphere radius, the micelle volume fraction and the corresponding expansion factors. A comparison of the appropriate quantities showed good agreement between the two techniques. SANS gave additional information e.g., volume fraction profiles for the micelles and volume fraction of water in the micelle core. Moderately concentrated solutions of copolymer E₉₀B₁₀ were studied in the gel state by small-angle X-ray scattering (SAXS) in tandem with rheology (oscillatory shear). Values for the dynamic elastic modulus (G′) of the gels significantly exceeded 10⁴ Pa across the range of temperature (25–80°C) and frequency (0.1–100 rad s^-1) explored. The SAXS patterns for the orientated gels showed them to have a body-centred-cubic structure, as expected for packed, spherical micelles. This structure persisted over a wide concentration range, e.g., until crystallisation of the E blocks occurred at high concentration (⩾70 wt.% copolymer). By combining the present and published results, a comparison was made of the micelle and gel properties of copolymers with the same B-block length but different E-block lengths, i.e., E₉₀B₁₀, E₄₀B₁₀ and E₁₈B₁₀. As would be expected, as the E-block length was increased, the micelle association numbers decreased while the micelle radii and expansion factors increased. The critical gel concentration (cgc) also decreased as the E-block length was increased. Moreover, the cgc correlated quantitatively with the thermodynamic expansion factors obtained by SLS and SANS from the exclusion properties of the micelles.

References

1. I. R. Schmolka and L. R. Bacon, J. Am. Oil Chem. Soc., 1967, 44, 559.
2. I. R. Schmolka, J. Biomed. Mater. Res., 1972, 6, 571.
3. P. C. Chen-Chow and S. G. Frank, Int. J. Pharm., 1981, 8, 89.
4. M. W. Edens, in Nonionic Surfactants: Polyoxyalkylene Block Copolymers, ed. V. M. Nace, Marcel Dekker Inc., New York, 1996, ch. 5.
5. B. Chu and Z.-K. Zhou, in Nonionic Surfactants: Polyoxyalkylene Block Copolymers, ed. V. M. Nace, Marcel Dekker Inc., New York, 1996, ch. 3.
6. K. Mortensen, J. Phys.: Condens. Matter, 1996, 8, A103.
7. P. Alexandridis, Curr. Opin. Colloid Interface Sci., 1997, 2, 478.
8. The Dow Chemical Co., Freeport, Texas, Technical Literature, B-Series Polyglycols. Butylene Oxide/Ethylene Oxide Block Copolymers, 1994.
9. V. M. Nace, J. Am. Oil Chem. Soc., 1996, 73, 1.
10. I. R. Schmolka, in Nonionic Surfactants, Surfactant Science Series, Vol. 1, ed. M. J. Schick, Marcel Dekker, New York, 1967, ch. 10.
11. W.-B. Sun, J.-F. Ding, R. H. Mobbs, D. Attwood and C. Booth, Colloids Surf., 1991, 54, 103.
12. Y.-Z. Luo, C. V. Nicholas, D. Attwood, J. H. Collett, C. Price and C. Booth, Colloid Polym. Sci., 1992, 270, 1094.
13. C. Booth, G.-E. Yu and V. M. Nace, in Amphiphilic Block Copolymers. Self-assembly and Applications, ed. P. Alexandridis and B. Lindman, Elsevier, Amsterdam, in press.
14. N.-J. Deng, Y.-Z. Luo, S. Tanodekaew, N. Bingham, D. Attwood and C. Booth, J. Polym. Sci., Part B; Polym. Phys., 1995, 33, 1085.
15. I. W. Hamley, J. A. Pople, J. P. A. Fairclough, A. J. Ryan, C. Booth and Y.-W. Yang, Macromolecules, 1998, 31, 3906.
16. I. W. Hamley, J. A. Pople, C. Booth, Y.-W. Yang and S. M. King, Langmuir, 1998, 14, 3182.
17. I. W. Hamley, J. A. Pople, C. Booth, L. Derici, M. Impéror-Clerc and P. Davidson, Phys. Rev. E: Stat. Phys., Plasmas, Fluids, Relat. Interdiscip. Top., 1998, 58, 7620.
18. J. A. Pople, I. W. Hamley, J. P. A. Fairclough, A. J. Ryan, B. U. Komanschek, A. J. Gleeson, G.-E. Yu and C. Booth, Macromolecules, 1997, 30, 5721.
19. I. W. Hamley, J. A. Pople, J. P. A. Fairclough, N. J. Terrill, A. J. Ryan, G.-E. Yu, C. Booth, O. Diat, K. Almdal, K. Mortensen and M. Vigild, J. Chem. Phys., 1998, 108, 6929.
20. J. A. Pople, I. W. Hamley, N. J. Terrill, J. P. A. Fairclough, A. J. Ryan, G.-E. Yu and C. Booth, Polymer, 1998, 39, 4891.
21. I. W. Hamley, J. A. Pople and O. Diat, Colloid Polym. Sci., 1998, 276, 446.
22. G.-E. Yu, Y.-W. Yang, Z. Yang, D. Attwood, C. Booth and V. M. Nace, Langmuir, 1996, 12, 3404.
23. J. A. Pople, I. W. Hamley, J. P. A. Fairclough, A. J. Ryan and C. Booth, Macromolecules, 1998, 31, 2592.
24. J. A. Pople, I. W. Hamley and G. P. Diakun, Rev. Sci. Instrum., 1998, 69, 3015.
25. J. A. Pople, I. W. Hamley, J. P. A. Fairclough, A. J. Ryan, G. Hill and C. Price, Polymer, accepted.
26. M. Weston, J. P. A. Fairclough and A. J. Ryan, in preparation.
27. P. Alexandridis, U. Olsson and B. Lindman, Langmuir, 1997, 13, 23.
28. A. D. Bedells, R. M. Arafeh, Z. Yang, D. Attwood, F. Heatley, J. C. Padget, C. Price and C. Booth, J. Chem. Soc., Faraday Trans., 1993, 89, 1235.
29. G.-E. Yu, Z. Yang, M. Ameri, D. Attwood, J. H. Collett, C. Price and C. Booth, J. Phys. Chem. B, 1997, 101, 4394.
30. F. Heatley, G.-E. Yu, W.-B. Sun, E. J. Pywell, R. H. Mobbs and C. Booth, Eur. Polym. J., 1990, 26, 583.
31. Y.-W. Yang, N.-J. Deng, G.-E. Yu, Z.-K. Zhou, D. Attwood and C. Booth, Langmuir, 1995, 11, 4703.
32. Y.-W. Yang, Z. Yang, Z.-K. Zhou, D. Attwood and C. Booth, Macromolecules, 1996, 29, 670.
33. Z. Yang, Y.-W. Yang, Z.-K. Zhou, D. Attwood and C. Booth, J. Chem. Soc., Faraday Trans., 1996, 92, 257.
34. S. W. Provencher, Makromol. Chem., 1979, 180, 201.
35. J. S. Pedersen, J. Phys. IV, 1993, 3, 491.
36. J. S. Pedersen, in Modern Aspects of Small-Angle Scattering, ed. H. Brumberger, Kluwer Academic Publishers, Dordrecht, 1995, p. 57.
37. H. Li, G.-E. Yu., C. Price, C. Booth, E. Hecht and H. Hoffmann, Macromolecules, 1997, 30, 1347.
38. N. Bliss, J. Bordas, B. D. Fell, N. W. Harris, W. I. Helsby, G. R. Mant, W. R. Smith and E. Towns-Andrews, Rev. Sci. Instrum., 1995, 66, 1311.
39. A. Kelarakis, V. Havredaki, G.-E. Yu, L. Derici and C. Booth, Macromolecules, 1998, 31, 944.
40. D. Attwood, J. H. Collett and C. J. Tait, Int. J. Pharm., 1985, 26, 25.
41. S.-M. Mai, C. Booth and V. M. Nace, Eur. Polym. J., 1997, 33, 991.
42. H. Vink, J. Chem. Soc., Faraday Trans. 1, 1985, 81, 1725; see also J. Selser, in Light Scattering, Principles and Development, ed. W. Brown, Clarendon Press, Oxford, 1996, p. 237.
43. A. Vrij, J. Chem. Phys., 1978, 69, 1742.
44. N. F. Carnahan and K. E. Starling, J. Chem. Phys., 1969, 51, 635.
45. J. S. Pedersen and M. C. Gerstenberg, Macromolecules, 1996, 29, 1363.
46. M. C. Gerstenberg, PhD Thesis, Risø National Laboratory, Denmark; Report Risø-R-986(EN) available on request to Risø Library.
47. K. Mortensen and J. S. Pedersen, Macromolecules, 1993, 26, 805.
48. J. K. Percus and G. J. Yevick, J. Phys. Rev., 1958, 110, 1.
49. J. S. Pedersen, D. Posselt and K. Mortensen, J. Appl. Crystallogr., 1996, 23, 321.
50. J. S. Pedersen, Adv. Colloid Interface Sci., 1997, 70, 171.
51. C. Booth and D. R. Beech, J. Polym. Sci., Polym. Phys. Ed., 1969, 7, 575.
52. C. Booth and R. Orme, Polymer, 1970, 11, 626.
53. P. J. Flory, Statistical Mechanics of Chain Molecules, Interscience, New York, 1969, p. 165.
54. J. S. Pedersen, unpublished results.
55. I. Goldmints, F. K. von Gotttenberg, K. A. Smith and T. A. Hatton, Langmuir, 1997, 13, 3659.
56. I. Goldmints, G.-E. Yu, C. Booth, K. A. Smith and T. A. Hatton, Langmuir, 1999, 15, 1651.
57. Y.-C. Liu, S.-H. Chen and J. S. Huang, Macromolecules, 1998, 31, 2236.
58. J. S. Pedersen, I. W. Hamley and P. Linse, unpublished results.
59. H. Altinok, S. K. Nixon, P. A. Gorry, D. Attwood, C. Booth, A. Kelarakis and V. Havredaki, Colloids Surf., B, accepted.
60. A. D. Bedells, R. M. Arafeh, Z. Yang, D. Attwood, J. C. Padget, C. Price and C. Booth, J. Chem. Soc., Faraday Trans., 1993, 89, 1243.
61. M. Malmsten and B. Lindman, Macromolecules, 1992, 25, 5440.
62. S. Hvidt, E. B. Jørgensen, W. Brown and K. Schillen, J. Phys. Chem., 1994, 98, 12320.
63. G. Wanka, H. Hoffmann and W. Ulbricht, Macromolecules, 1994, 27, 4145.
64. G.-E. Yu, Y.-L. Deng, S. Dalton, Q.-G. Wang, D. Attwood, C. Price and C. Booth, J. Chem. Soc., Faraday Trans., 1992, 88, 2537.
65. P. Bahadur and K. Pandya, Langmuir, 1992, 8, 2666.
66. E. B. Jørgensen, S. Hvidt, W. Brown and K. Schillen, Macromolecules, 1997, 30, 2355.
67. P. Bahadur, K. Pandya, M. Almgren, P. Li and P. Stilbs, Colloid Polym. Sci., 1993, 271, 657.
68. Y.-L. Deng, C. Price and C. Booth, Eur. Polym. J., 1994, 30, 103.
69. M. Almgren, W. Brown and S. Hvidt, Colloid Polym. Sci., 1995, 273, 2.
70. A. Kelarakis, V. Havredaki, L. Derici, G.-E. Yu, C. Booth and I. W. Hamley, J. Chem. Soc., Faraday Trans., 1998, 94, 3639.
71. Y.-W. Yang, S. Tanodekaew, S.-M. Mai, C. Booth, A. J. Ryan, W. Bras and K. Viras, Macromolecules, 1995, 28, 6029.
72. I. W. Hamley, J. A. Pople, M. Ameri, D. Attwood, C. Booth and A. J. Ryan, Macromol. Chem. Phys., 1998, 199, 1753.
73. I. W. Hamley, J. A. Pople, M. Ameri, D. Attwood and C. Booth, Colloids and Surf. A, 1998, 145, 185.
74. K. Mortensen, W. Brown and E. B. Jørgensen, Macromolecules, 1995, 28, 1458.
75. M. Portmann, E. H. Landau and P. L. Luisi, J. Phys. Chem., 1991, 95, 8437.
76. J. P. A. Fairclough, A. J. Ryan, I. W. Hamley, H. Li, G.-E. Yu and C. Booth, Macromolecules, 1999, 32, 2058.
77. Y.-W. Yang, Z. Ali-Adib, N. B. McKeown, A. J. Ryan, D. Attwood and C. Booth, Langmuir, 1997, 13, 1860.
78. C. P. Buckley and A. J. Kovacs, Prog. Colloid Polym. Sci., 1975, 58, 44.
79. S. G. Yeates, H. H. Teo, R. H. Mobbs and C. Booth, Makromol. Chem., 1984, 185, 1559.
80. D. J. Mitchell, G. J. T. Tiddy, L. Waring, T. Bostock and M. P. McDonald, J. Chem. Soc., Faraday Trans., 1983, 79, 975.
81. I. W. Hamley, K. Mortensen, G.-E. Yu and and C. Booth, Macromolecules, 1998, 31, 6958.
82. G. A. McConnell, A. P. Gast, J. S. Huang and S. D. Smith, Phys. Rev. Lett., 1993, 71, 2102.
83. M. O. Robbins, K. Kremer and G. S. Grest, J. Chem. Phys., 1988, 88, 3286; Y. Monovoukas and A. P. Gast, J. Colloid Interface Sci., 1989, 128, 533.
84. G. A. McConnell, E. K. Lin, A. P. Gast, J. S. Huang, M. Y. Lin and S. D. Smith, Faraday Discuss., 1994, 98, 121.