Crystal structure of the microporous titanosilicate ETS-10 refined from single crystal X-ray diffraction data

Abstract

ETS-10 crystals up to 45 µm in size have been synthesized at 240 °C under a pressure of 80 MPa and the structure refined from single crystal X-ray diffraction data.

References

1. M. Taramasso, G. Perego and B. Notari, US Pat. 4410501, 1983.
2. S. M. Kuznicki, US Pat. 4853202, 1989.
3. S. M. Kuznicki, K. A. Thrush, F. M. Allen, S. M. Levine, M. M. Hamil, D. T. Hayhurst and M. Mansour, Synth. Micopor. Mater., 1992, 1, 427.
4. V. Valtchev and S. Mintova, Zeolites, 1994, 14, 697.
5. M. W. Anderson, O. Terasaki, T. Ohsuna, P. J. O. Malley, A. Philippou, S. P. Mackay, A. Ferreira, J. Rocha and S. Lidin, Nature, 1994, 367, 347.
6. M. W. Anderson, O. Terasaki, T. Ohsuna, P. J. O. Malley, A. Philippou, S. P. Mackay, A. Ferreira, J. Rocha and S. Lidin, Philos. Mag. B, 1995, 71, 813.
7. R. J. Davis, Z. Liu, J. E. Tabora and W. S. Wieland, Catal. Lett., 1995, 34, 101.
8. R. Carli, C. L. Bianchi and V. Ragaini, Catal. Lett., 1995, 33, 49.
9. T. K. Das, A. J. Chandwadkar and S. Sivasanker, J. Mol. Catal., 1996, 107, 199.
10. X. Yang and R. E. Truitt, J. Phys. Chem., 1996, 100, 3713.
11. X. Liu and J. K. Thomas, Chem. Commun., 1996, 1435.
12. M. E. Grillo and J. Carrazza, J. Phys. Chem., 1996, 100, 12 261.
13. G. Sankar, R. G. Bell, J. M. Thomas, M. W. Anderson, P. A. Wright and J. Rocha, J. Phys. Chem., 1996, 100, 449.
14. M. E. Grillo and J. Carrazza, J. Phys. Chem., 1997, 101, 6749.
15. E. Borello, C. Lamberti, S. Bordiga and C. O. Arean, Appl. Phys. Lett., 1997, 71, 2319.
16. T. K. Das, A. J. Chandwadkar and S. Sivasanker, Catal. Lett., 1997, 44, 113.
17. S. Ganapathy, T. K. Das, R. Vertrivel, S. S. Ray, T. Sen, S. Sivasanker, L. Delevoye, C. Fernandez and J. P. Amoureux, J. Am. Chem. Soc., 1998, 120, 4752.
18. J. Rocha, A. Ferreira, Z. Lin and M. W. Anderson, Micropor. Mesopor. Mater., 1998, 23, 253.