Electrochemical lithium insertion in a cation deficient thiospinel Cu_3.31GeFe₄Sn₁₂S₃₂

Abstract

We present the characterization and the electrochemical study of the cation deficient thiospinel Cu_3.31GeFe₄Sn₁₂S₃₂ as a cathodic material in lithium cells. The pristine compound has a spinel-related structure, where the copper defect in the tetrahedral site induces a partial oxidation of Fe^II to Fe^III. The discharge curve shows the presence of several insertion steps. The reduction of Fe^III to Fe^II and a copper extraction takes place during the first and second steps, respectively. Moreover, the lithium insertion originates a first-order spinel to rocksalt transition, indicated by the third step of the discharge curve. Finally, at low voltages (<1.65 V) a Sn^IV to Sn^II reduction takes place.

References

1. M. Eisenberg, J. Electrochem. Soc., 1980, 127, 2382.
2. M. M. Thackeray, W. I. F. David and J. B. Goodenough, Mater. Res. Bull., 1982, 17, 785.
3. R. Schöllhorn and A. Payer, Angew. Chem., Int. Ed. Engl., 1985, 24, 67.
4. S. Sinha and D. W. Murphy, Solid State Ionics, 1986, 20, 81.
5. A. C. W. P. James, J. B. Goodenough, N. J. Clayden and P. M. Banks, Mater. Res. Bull., 1989, 24, 143.
6. A. C. W. P. James, B. Ellis and J. B. Goodenough, Solid State Ionics, 1988, 27, 45.
7. N. Imanishi, K. Inoue, Y. Takeda and O. Yamamoto, J. Power Sources, 1993, 43–44, 1993.
8. P. de la Mora and J. B. Goodenough, J. Solid State Chem., 1987, 70, 121.
9. P. Lavela, J. L. Tirado, J. Morales, J. Olivier-Fourcade and J. C. Jumas, J. Mater. Chem., 1996, 6, 41.
10. K. Ruebenbauer and T. Birchall, Hyperfine Interact., 1979, 7, 125.
11. D. B. Wiles and R. A. Young, J. Appl. Crystallogr., 1995, 28, 366.
12. M. Womes, J. C. Jumas, J. Olivier-Fourcade, F. Aubertin and U. Gonser, Chem. Phys. Lett., 1993, 201, 555.
13. C. Branci, J. Sarradin, J. Olivier-Fourcade and J. C. Jumas, Mol. Cryst. Liq. Cryst., in press.