Thermal stability of styrene grafted and sulfonated proton conducting membranes based on poly(vinylidene fluoride)

Abstract

The thermal stability of styrene grafted and sulfonated poly(vinylidene fluoride), PVDF-g-PSSA, proton conducting membranes has been studied using thermal gravimetric analysis in combination with mass spectrometry and thermochromatography. The matrix polymer, PVDF, and the non-sulfonated counterpart, PVDF-g-PS, were studied as reference materials. It was found that the degradation of the PVDF-g-PS membrane proceeds in two steps starting atca. 340 °C with the evolution of degradation products typical of polystyrene. The PVDF-g-PSSA membranes are stable to around 270 °C even in a strongly oxidising atmosphere. The degradation starts with the simultaneous evolution of water and sulfur dioxide. The polystyrene grafts start decomposing at 340 ^oC in the PVDF-g-PSSA membranes. Thus the membranes are suitable for tests in electrochemical applications at elevated temperatures.

References

1. Fuel Cell Handbook, ed. A. J. Appleby and R. L. Foulkes, Van Nostrand, New York, 1989; G. G. Scherer, Ber. Bunsenges. Phys. Chem., 1990, 94, 1008.
2. N. G. Polyanskii and P. E. Tulupov, Russ. Chem. Rev., 1971, 40, 1030.
3. A. Bozzi and A. Chapiro, Eur. Polym. J., 1987, 23, 255.
4. A. Chapiro, Radiat. Phys. Chem., 1979, 9, 55.
5. A. Bozzi and A. Chapiro, Radiat. Phys. Chem., 1988, 32, 193.
6. B. D. Gupta and A. Chapiro, Eur. Polym. J., 1989, 11, 1137.
7. B. D. Gupta and A. Chapiro, Eur. Polym. J., 1989, 11, 1145.
8. E. A. Hegazy, I. Ishigaki, A. M. Dessouki, A. Rabie and J. Okamoto, J. Appl. Polym. Sci., 1982, 27, 535.
9. A. Chapiro and A. M. Jedrychowska-Bonamour, Eur. Polym. J., 1984, 20, 1079.
10. M. V. Rouilly, R. Kötz, O. Haas, G. G. Scherer and A. Chapiro, J. Membr. Sci., 1993, 81, 89.
11. B. Gupta and G. G. Scherer, J. Appl. Polym. Sci., 1993, 50, 2129.
12. B. Gupta, J. G. Highfield and G. G. Scherer, J Appl. Polym. Sci., 1994, 51, 1659.
13. S. Holmberg, T. Lehtinen, J. Näsman, D. Ostrovskii, M. Paronen, R. Serimaa, F. Sundholm, G. Sundholm, L. Torell and M. Torkkeli, J. Mater. Chem., 1996, 6, 1309.
14. S. Hietala, S. Holmberg, M. Karjalainen, J. Näsman, M. Paronen, R. Serimaa, F. Sundholm and S. Vahvaselkä, J. Mater. Chem., 1997, 7, 721.
15. T. Lehtinen, F. Sundholm, G. Sundholm, P. Björnbom and M. Bursell, Electrochim. Acta, accepted.
16. S. Holmberg, J. H. Näsman and F. Sundholm, Polym. Adv. Technol., accepted.
17. M. Kaljurand and M. Koel, Computerized Multiple Input Chromatography, Ellis Horwood, Chichester 1989, p. 139.
18. M. Elomaa, PhD Thesis, University of Helsinki, Helsinki 1991.
19. D. R. Deans, J. Chromatogr., 1984, 289, 43.
20. S. Hietala, E. Skou and F. Sundholm, submitted to Polymer.
21. B. Gupta and G. G. Scherer, Angew. Makromol. Chem., 1993, 210, 151.
22. T. Momose, I. Ishigaki and J. Okamoto, J. Appl. Polym. Sci., 1988, 36, 669.
23. F. N. Büchi, B. Gupta, O. Haas and G. G. Scherer, J. Electrochem. Soc., 1995, 142, 3044.
24. F. N. Büchi, B. Gupta, O. Haas and G. G. Scherer, Electrochim. Acta, 1995, 40, 345.
25. J. Brandrup and E. H. Immergut, Polymer Handbook, Wiley, New York, 3rd edn., 1989, p. VI-226 and VI-258.
26. R. Wiley and G. Mayberry, J. Polym. Sci. A, 1963, 1, 217.
27. C. F. Cullis and M. M. Hirschler, The Combustion of Organic Polymers, Clarendon, Oxford, 1981, pp. 229–230.
28. X. Zhu, M. Elomaa, F. Sundholm and C. H. Lochmüller, Macromol. Chem. Phys., 1997, 198, 3137.
29. T. A. Zawodzinski, Jr., M. Neeman, L. O. Sillerud and S. Gottesfeld, J. Phys. Chem., 1991, 95, 6040.
30. S. Hietala, S. Holmberg, J. Näsman, D. Ostrovskii, M. Paronen, R. Serimaa, F. Sundholm, L. Torell and M. Torkkeli, Appl. Macromol. Chem. Phys., 1997, 253, 151.