Synthesis of carbon nanotube–Fe-Al₂O₃ nanocomposite powders by selective reduction of different Al_1.8Fe_0.2O₃ solid solutions

Abstract

Al_1.8Fe_0.2O₃ solid solutions have been prepared as amorphous, η (cubic) and α (corundum) phases. The oxides have been reduced in a H₂–CH₄ gas mixture at 900 or 1000 °C, giving rise to composite powders containing alumina, α- and γ-Fe, Fe₃C and different forms of carbon including nanotubes, thick tubes and spheroidal particles. The powders have been investigated using a combination of chemical analysis, X-ray diffraction, Mössbauer spectroscopy, scanning and transmission electron microscopy, thermogravimetric analysis and specific surface area measurements. Using the stable form (corundum) of Al_1.8Fe_0.2O₃ as starting material favours the formation of carbon nanotubes compared to the other forms of carbon. This could partly result from the fact that the metal nanoparticles formed upon reduction of the α solid solution, which act as a catalyst for CH₄ decomposition and possibly nanotube nucleation, are smaller than when using amorphous or η solid solutions. Moreover, the crystallization of these latter compounds during the reduction in some way provokes the entrapment of carbon within the oxide grains. The nanotubes, most of which are less than 10 nm in diameter, are arranged in bundles several tens of micrometers long.

References

1. S. Iijima, Nature (London), 1991, 354, 56.
2. T. W. Ebbesen and P. M. Ajayan, Nature (London), 1992, 358, 220.
3. S. Iijima and T. Ichihashi, Nature (London), 1993, 363, 603.
4. D. S. Bethune, C. H. Kiang, M. S. de Vries, G. Gorman, R. Savoy, J. Vazquez and R. Beyers, Nature (London), 1993, 363, 605.
5. C. H. Kiang, W. A. Goddard, R. Beyers, J. R. Salem and D. Bethune, J. Phys. Chem. Solids, 1996, 57, 35.
6. S. Seraphin and D. Zhou, Appl. Phys. Lett., 1994, 64, 2087.
7. T. W. Ebbesen, H. J. Lezec, H. Hiura, J. W. Bennett, H. F. Ghaemi and T. Thio, Nature (London), 1996, 382, 54.
8. C. Guerret-Plecourt, Y. Le Bouar, A. Loiseau and H. Pascard, Nature (London), 1994, 372, 761.
9. A. Thess, R. Lee, P. Nikolaev, H. Dai, P. Petit, J. Robert, D. T. Colbert, C. Xu, Y. H. Lee, S. G. Kim, A. G. Rinkler, D. T. Colbert, G. E. Scuseria, D. Tomanek, J. E. Fisher and R. E. Smalley, Science, 1996, 273, 483.
10. S. Witanachchi and P. Mukherjee, J. Vac. Sci. Technol. A, 1995, 3, 1171.
11. M. J. Yacaman, M. M. Yoshida, L. Rendon and J. G. Santiesteban, Appl. Phys. Lett., 1993, 62, 657.
12. R. T. K. Baker and N. Rodriguez, Mater. Res. Soc. Symp. Proc., 1994, 349, 251.
13. S. Herreyre and P. Gadelle, Carbon, 1995, 33, 234.
14. V. Ivanov, A. Fonseca, J. B. Nagy, A. Lucas, P. Lambin, D. Bernaerts and X. B. Zhang, Carbon, 1995, 33, 1727.
15. K. Hernadi, A. Fonseca, J. B. Nagy, D. Bernaerts, J. Riga and A. Lucas, Synth. Met., 1996, 77, 31.
16. A. Fonseca, K. Hernadi, J. B. Nagy, Ph. Lambin and A. Lucas, Carbon, 1995, 33, 1759.
17. M. Endo, K. Takeuchi, K. Kobori, K. Takahashi, H. W. Kroto and A. Sarkar, Carbon, 1995, 33, 873.
18. A. Thess, R. Lee, P. Nikolaev, H. Dai, P. Petit, J. Robert, D. T. Colbert, C. Xu, Y. H. Lee, S. G. Kim, A. G. Rinkler, D. T. Colbert, G. E. Scuseria, D. Tomanek, J. E. Fisher and R. E. Smalley, Science, 1996, 273, 483.
19. A. Peigney, Ch. Laurent, F. Dobigeon and A. Rousset, J. Mater. Res., 1997, 12, 613.
20. X. F. Zhang, X. B. Zhang, G. Van Tendeloo, S. Amelinckx, M. Op De Beeck and J. Van Landuyt, J. Crystal Growth, 1993, 130, 368.
21. P. J. Harris, Eur. Microsc. Anal., 1994, 9, 13.
22. G. Hu, X. F. Zhang, D. P. Yu, S. Q. Feng, W. Xu and Z. Zhang, Solid State Commun., 1996, 98, 547.
23. D. Ugarte, Microsc. Microanal. Microstruct., 1993, 4, 505.
24. L. A. Bursill, J. L. Peng and X. D. Fan, Philos. Mag. A, 1995, 71, 1161.
25. S. J. Tans, M. H. Devoret, H. Dai, A. Thess, R. E. Smalley, L. J. Geerligs and C. Dekker, Nature (London), 1997, 386, 474.
26. A. Y. Kasumov, I. I. Khodos, P. M. Ajayan and C. Colliex, Europhys. Lett., 1996, 34, 429.
27. Y. Nakayama, S. Akita and Y. Shimada, Jpn. J. Appl. Phys., 1995, 34, L10.
28. H. Dai, E. W. Wong and C. M. Lieber, Science, 1996, 272, 523.
29. L. Langer, L. Stockman, J. P. Heremans, V. Bayot, C. H. Olk, C. Van Haesendonck, Y. Bruynserade and J. P. Issi, J. Mater. Res., 1994, 9, 927.
30. X. K. Wang, R. P. H. Chang, A. Pataashinski and J. B. Ketterson, J. Mater. Res., 1994, 9, 1578.
31. D. H. Robertson, D. W. Brenner and J. W. Mintmire, Phys. Rev. B, 1992, 45, 12 592.
32. W. A. De Heer, W. S. Bacsa, A. Chatelain, T. Gerfin, R. Humfrey-Baker, L. Forro and D. Ugarte, Science, 1995, 268, 845.
33. R. Seshadri, A. Govindaraj, H. N. Aiyer, R. Sen, G. N. Subbanna, A. R. Raju and C. N. R. Rao, Curr. Sci., 1994, 66, 839.
34. S. B. Sinnott, C. T. White and D. W. Brenner, Mater. Res. Soc. Symp. Proc., 1995, 359, 241.
35. M. M. J. Treacy, T. W. Ebbesen and J. M. Gibson, Nature (London), 1996, 381, 678.
36. S. Iijima, C. Brabec, A. Maiti and J. Bernholc, J. Chem. Phys., 1996, 104, 2089.
37. J. F. Despres, E. Daguerre and K. Lafdi, Carbon, 1995, 33, 87.
38. K. Tohji, T. Goto, H. Takahashi, Y. Shinoda, N. Shimizu, B. Jeyadevan, I. Matsuoka, Y. Saito, A. Kasuhka, T. Oshuna, K. Hiraga and Y. Nishina, Nature (London), 1996, 383, 679.
39. R. T. K. Baker, P. S. Harris, R. B. Thomas and R. J. Waite, J. Catal., 1993, 30, 86.
40. A. Oberlin, M. Endo and T. Koyama, J. Crystal Growth, 1976, 32, 335.
41. K. Hernadi, A. Fonseca, J. B. Nagy, D. Bernaerts, A. Fudala and A. A. Lucas, Zeolites, 1996, 17, 416.
42. X. Devaux, Ch. Laurent and A. Rousset, Nanostruct. Mater., 1993, 2, 339.
43. O. Quénard, Ch. Laurent, M. Brieu and A. Rousset, Nanostruct. Mater., 1996, 7, 497.
44. Ch. Laurent, A. Rousset, M. Verelst, K. R. Kannan, A. R. Raju and C. N. R. Rao, J. Mater. Chem., 1993, 3, 513.
45. M. Verelst, K. R. Kannan, G. N. Subbanna, C. N. R. Rao, Ch. Laurent and A. Rousset, J. Mater. Res., 1992, 7, 3072.
46. X. Devaux, Ch. Laurent, M. Brieu and A. Rousset, J. Alloys Compd., 1992, 188, 179.
47. A. Marchand, X. Devaux, B. Barbara, P. Mollard, M. Brieu and A. Rousset, J. Mater. Sci., 1993, 28, 2217.
48. A. Rousset and J. Paris, Bull. Soc. Chim. Fr., 1967, 10, 388.
49. D. Wagmann, J. E. Kilpatrick, W. J. Taylor, K. S. Pitzer and F. D. Rossini, J. Res. Natl. Bur. Stand., 1945, 34, 143.
50. Ch. Laurent, J. J. Demai, A. Rousset, K. R. Kannan and C. N. R. Rao, J. Mater. Res., 1994, 9, 229.
51. H. L. Yakel, Int. Met. Rev., 1985, 30, 17.
52. G. Le Caër, J. M. Dubois and J. P. Sénateur, J. Solid State Chem., 1976, 19, 19.
53. X. X. Bi, B. Ganguly, G. P. Huffman, F. E. Huggins, M. Endo and P. C. Eklund, J. Mater. Res., 1993, 8, 1666.
54. O. Quénard, E. De Grave, Ch. Laurent and A. Rousset, J. Mater. Chem., 1997, 7, 2457.
55. R. T. K. Baker, J. R. Alonzo, J. A. Dumesic and D. J. C. Yates, J. Catal., 1977, 74, 82.
56. Y. Saito, Carbon, 1995, 33, 979.
57. Ch. Laurent, Ch. Blaszczyk, M. Brieu and A. Rousset, Nanostruct. Mater., 1995, 6, 317.
58. P. L. Walker, Jr., J. F. Rakszawski and G. R. Imperial, J. Phys. Chem., 1959, 63, 133.
59. P. L. Walker, Jr., J. F. Rakszawski and G. R. Imperial, J. Phys. Chem., 1959, 63, 140.
60. N. M. Rodriguez, M.-S. Kim and R. T. K. Baker, J. Phys. Chem., 1994, 98, 13 108.
61. W. B. Downs and R. T. K. Baker, J. Mater. Res., 1995, 10, 625.