Synthesis of yttrium aluminium garnet by the citrate gel process

Abstract

We describe the synthesis of polycrystalline yttrium aluminium garnet (YAG) by the citrate gel process. The conditions for obtaining the pure phase have been determined and the YAG powders were characterized by X-ray diffraction, IR spectroscopy and transmission electron microscopy. YAG powders were obtained at significantly lower temperatures than by other conventional techniques. Moreover, the particle size of the powders prepared through this process is in the range 20–70 nm, depending on the thermal treatment. The lattice parameter of the YAG powders was also determined and we observed that the lattice parameter depends on the particle size. An explanation for this behaviour is provided.

References

1. G. de With and H. J. A. van Dijk, Mater. Res. Bull., 1984, 19, 1669.
2. K. Ohno and T. Abe, J. Electrochem. Soc., 1994, 141, 1252.
3. R. P. Rao, J. Electrochem. Soc., 1996, 143, 189.
4. N. J. Hess and G. J. Exarhos, J. Non-Cryst. Solids, 1994, 178, 91.
5. P. Apte, H. Burke and H. Pickup, J. Mater. Res., 1992, 7, 706.
6. M. Sekita, H. Haneda, T. Yanaginati and S. Shirasaki, J. Appl. Phys., 1990, 67, 453.
7. O. Yamaguchi, K. Takeoka, K. Hirota, H. Takano and A. Hayashida, J. Mater. Sci., 1992, 27, 1291.
8. P. Vaqueiro, M. P. Crosnier-Lopez and M. A. López-Quintela, J. Solid State Chem., 1996, 126, 161.
9. C. Marcilli, P. Courty and B. Delmon, J. Am. Ceram. Soc., 1970, 53, 56.
10. M. P. Pechini, US Pat. No. 3, July 1967, 330, 697.
11. K. Kakihana, J. Sol Gel Sci. Technol., 1996, 6, 7.
12. Joint Committee on Powder Diffraction Standard, Swarthmore, Pennsylvania, PA.
13. Th. H. De Keijser, J. L. Langford, E. J. Mittemeijer and A. B. P. Vogels, J. Appl. Cryst., 1982, 15, 308.
14. J. Rodríguez-Carvajal, Institut Laue-Langevin, 1988.
15. B. Rupp, Scr. Metall., 1988, 22, 1.
16. J. I. Langford, National Institute of Standards and Technology Special Publication 846. Proceedings of the International Conference Accuracy in Powder DiVraction II, 1992.
17. P. Ayyub, M. Multani, M. Barma, V. R. Palkar and R. Vijayaraghavan, J. Phys. C: Solid State Phys., 1988, 21, 2229.
18. R. Lamber, S. Wetjen and N. I. Jaeger, Phys. Rev. B, 1995, 51, 10 968.
19. M. Y. Gamarnik and Y. Y. Sidorin, Phys. Status Solidi B, 1989, 156, K1.
20. P. Ayyub, V. R. Palkar, S. Chattopadhyay and M. Multani, Phys. Rev. B, 1995, 51, 6135.
21. D. Schoeer and R. C. Nininger, Phys. Rev. Lett., 1967, 19, 632.
22. X. D. Liu, H. Y. Zhang, K. Lu and Z. Q. Hu, J. Phys.: Condens. Matter., 1994, 6, L497.
23. M. Y. Gamarnik, Phys. Status Solidi B, 1991, 164, 107.
24. B. M. Gatehouse, S. E. Livingstone and R. S. Nyholm, J. Chem. Soc., 1958, 3137.
25. A. M. Hofmeister and K. R. Campbell, J. Appl. Phys., 1992, 72, 638.