Magnetic properties of two-dimensional triangular arrays of Ni ions in nickel phyllosilicates

Abstract

Synthetic phyllosilicates, with nickel replacing the magnesium atoms, have been prepared under autogenous pressures at 220 °C. Both 1:1 phyllosilicate, having interlayer spacing of 7 Å, and 2:1 phyllosilicate with 9.4 Å spacing were obtained depending on the metal to silicon ratio. The latter was also expanded to 13.2 Å by use of an amine substituted silicon alkoxide. Dissolution of the silicate precursors was achieved in the presence of fluoride as NH₄F or HF. The microcrystalline products were characterised by X-ray diffraction, thermal analysis, transmission microscopy and chemical analyses. All the samples show long range ferromagnetic order below 28 K accompanied by a rounded maximum in the specific heat measurements. At 4 K they show hysteresis in the magnetisation, with a remnant value ranging from 0.8 to 1.5 µ_B depending on orientation of the applied field and coercive fields up to 3240 Oe.

References

1. J. S. Miller and A. J. Epstein, Angew. Chem., Int Ed. Engl., 1994, 33, 385.
2. D. Gatteschi, Adv. Mater., 1994, 6, 635.
3. O. Kahn, Molecular Magnetism, VCH, New York, 1993.
4. O. Kahn and Y. Journaux, in Inorganic Materials, ed. D. W. Bruce and D. O'Hare, Wiley, New York, 1993.
5. A. Abragam and B. Bleaney, Electron Paramagnetic Resonance of Transition Metal Ions, Clarendon Press, New York, 1970.
6. W. Reiff, B. C. Dodrill and C. C. Torardi, Mol. Cryst. Liq. Cryst., 1995, 274, 137.
7. G. A. Martin, A. Renourez, G. Dalmai-Imelink and B. Imelink, J. Chim. Phys., 1970, 67, 1149.
8. C. S. Anderson and S. W. Bailey, Am. Mineral., 1981, 66, 185.
9. T. F. Semenova, I. V. Rozhdestvenskaya and V. A. Frank-Kamenetskii, Kristallografiya, 1977, 22, 1196.
10. G. A. Martin and J. A. Dalmon, C. R. Acad. Sci. Paris, Sér. B, 1971, 272, 304.
11. G. A. Martin, J. A. Dalmon, R. Dutartre, P. Turlier and J. C. Volta, J. Chim. Phys., 1972, 2, 277.
12. S. W. Bailey, Rev. Mineral., 1988, 19.
13. S. Rouba, Thesis of the Université Louis Pasteur de Strasbourg, 1996.