Characterisation of graphite nanoplatelets (GNP) prepared at scale by high-pressure homogenisation

Author affiliations

Abstract

Graphite nanoplatelets (GNP) were prepared by a high-pressure homogenisation process (HPHP) via exfoliation of bulk graphite, yielding GNP in the form of square shaped platelets with lateral dimensions on the micrometre (μm) scale and thicknesses on the nanometre (nm) scale (<200 nm). The platelets have a polycrystalline structure with d002 = 0.335 nm and L002 = 2 nm, with a low crystalline defect concentration confirmed by weak D and D′ bands in the Raman spectra. The shift in the G band from 1587 cm−1 (graphene) to 1580 cm−1 (GNP) and the asymmetric G′ band combined with a decrease in IG′/IG from 0.45 for the bulk graphite to 0.40 for the GNP confirmed a partially exfoliated structure. X-ray photoelectron spectroscopy (XPS) confirmed the presence of impurities on the GNP surface due to the surfactant used during the exfoliation process. Contact angle measurements (67° ± 2° (0 s), 64° ± 2° (10 s)) suggested the surface of the GNP was hydrophilic. The as produced GNP is a macro-porous material with sheet-like particles having non-uniform shape and size and a BET surface area of ca. 94 m2 g−1. The GNP is thermally stable under oxidative conditions up to 430 °C. The HPHP process is readily scalable and provides a cost effective route for the production of GNP.

Graphical abstract: Characterisation of graphite nanoplatelets (GNP) prepared at scale by high-pressure homogenisation

Back to tab navigation

Publication details

The article was received on 12 Mar 2019, accepted on 29 Apr 2019 and first published on 01 May 2019


Article type: Paper
DOI: 10.1039/C9TC01361J
J. Mater. Chem. C, 2019,7, 6383-6390

  •   Request permissions

    Characterisation of graphite nanoplatelets (GNP) prepared at scale by high-pressure homogenisation

    V. Guerra, C. Wan, V. Degirmenci, J. Sloan, D. Presvytis, M. Watson and T. McNally, J. Mater. Chem. C, 2019, 7, 6383
    DOI: 10.1039/C9TC01361J

Search articles by author

Spotlight

Advertisements