Designing lead-free bismuth ferrite-based ceramics learning from relaxor ferroelectric behavior for simultaneous high energy density and efficiency under low electric field

Author affiliations

Abstract

Bismuth ferrite (BiFeO3, BFO) possesses very large spontaneous polarization, which provides a great potential in dielectric energy-storage capacitors. However, the presence of large remanent polarization heavily restricts the achievement of excellent performance in the energy storage field. Herein we designed local compositional disorder and constructed quenched random fields to maximize the discrepancy between the maximum polarization and the remanent polarization by means of introducing Zn2+ and Ta5+ at B-sites together in BiFeO3-based solution. Interestingly, pinched-hysteresis loops were observed in this Ba(Zn1/2Ta2/3)O3-modified BFO-based solution. Ultrahigh recoverable energy density (2.56 J cm−3) was first reported under low electric field (16 kV mm−1), which is much superior to the previous results regarding BFO-based bulk ceramics. In addition, an excellent recoverable energy density (>2 J cm−3) and a high efficiency (>80%) were obtained simultaneously in this BZT-modified BFO-based bulk material under low electric field (<20 kV mm−1). These results demonstrate that the strategy of constructing weakly coupled polar structures is feasible and effective to boost the energy density and efficiency for BiFeO3-based bulk ceramics, which may pave a significant step towards utilizing energy-storage applications for BiFeO3-based materials.

Graphical abstract: Designing lead-free bismuth ferrite-based ceramics learning from relaxor ferroelectric behavior for simultaneous high energy density and efficiency under low electric field

Back to tab navigation

Supplementary files

Publication details

The article was received on 02 Aug 2018, accepted on 17 Sep 2018 and first published on 19 Sep 2018


Article type: Communication
DOI: 10.1039/C8TC03855D
Citation: J. Mater. Chem. C, 2018,6, 10211-10217

  •   Request permissions

    Designing lead-free bismuth ferrite-based ceramics learning from relaxor ferroelectric behavior for simultaneous high energy density and efficiency under low electric field

    N. Liu, R. Liang, Z. Zhou and X. Dong, J. Mater. Chem. C, 2018, 6, 10211
    DOI: 10.1039/C8TC03855D