Al–Sc dual-doped LiGe2(PO4)3 – a NASICON-type solid electrolyte with improved ionic conductivity

Author affiliations

Abstract

LiGe2(PO4)3 (LGP), a NASICON-type solid electrolyte, has many advantages such as its superior electrochemical and thermal stability for use in all solid-state lithium batteries. However, its low ionic conductivity is one of the challenges that can hinder its practical application commercially. In this work, the influence of adding different amounts of scandium and aluminum on the Li+ conductivity of LGP was investigated computationally and experimentally. Substituting 25% of Ge4+ ions in the LGP structure with Al3+ and/or Sc3+ ions to obtain doped LGP in the form of Li1+x+yAlxScyGe2−xy(PO4)3, where x + y = 0.5, led to more Li+ ions in the 36f vacant sites (M2) and resulted in enhanced ionic conductivity of the material. In both approaches, the highest bulk Li+ conductivity of 5.826 mS cm−1 was obtained for Li1.5Al0.33Sc0.17Ge1.5(PO4)3 from the experimental measurement. The activation energy was also investigated theoretically using the nudged elastic band method, and the lowest value (0.279 eV) was obtained for this composition. Furthermore, the Li1+x+yAlxScyGe2−xy(PO4)3 electrolytes were synthesized using a melt-quenching method and subsequently transformed into a glass–ceramic material through heat treatment. X-ray diffraction, electrochemical impedance spectroscopy and cyclic voltammetry were used to characterize the structure, measure the Li+ conductivity and determine the electrochemical window of the synthesized glass–ceramic material, respectively. There was a remarkable agreement between the computationally calculated and experimentally measured values of ionic conductivity, activation energy and electrochemical window. Finally, its applicability in a solid-state battery was tested, and it showed good electrochemical performance.

Graphical abstract: Al–Sc dual-doped LiGe2(PO4)3 – a NASICON-type solid electrolyte with improved ionic conductivity

Supplementary files

Article information


Submitted
13 Jan 2020
Accepted
02 May 2020
First published
07 May 2020

J. Mater. Chem. A, 2020,8, 11302-11313
Article type
Paper

Al–Sc dual-doped LiGe2(PO4)3 – a NASICON-type solid electrolyte with improved ionic conductivity

Y. Nikodimos, M. Tsai, L. H. Abrha, H. H. Weldeyohannis, S. Chiu, H. K. Bezabh, K. N. Shitaw, F. W. Fenta, S. Wu, W. Su, C. Yang and B. J. Hwang, J. Mater. Chem. A, 2020, 8, 11302 DOI: 10.1039/D0TA00517G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.


Social activity

Search articles by author

Spotlight

Advertisements