Copper manganese oxide enhanced nanoarray-based monolithic catalysts for hydrocarbon oxidation

Author affiliations

Abstract

Copper manganese oxide (CuMn2O4) was introduced into the nanoarray-based monolithic catalysts system for advanced exhaust after-treatment. Through scalable and cost-effective hydrothermal reactions, nanosheet layers of copper manganese oxide were uniformly coated onto the manganese oxide nanoarrays (HM-PCR), which were grown on the cordierite honeycomb monoliths. The core nanoarray support, HM-PCR, a well-defined array architecture for active material deposition, contributed to an increase of open surface area and thus enhanced catalytic oxidation performance. The CuMn2O4 coated nanoarray-based catalyst, NA-CuMn2O4, shows efficient 90% propane (C3H8) conversion at around 400 °C, which is 50 °C and 75 °C lower than CuMn2O4 wash-coated catalyst (WC-CuMn2O4) and Pd loaded catalyst (WC-Pd), respectively. Compared to monolithic catalysts with a traditional alumina support, the benefit of nanoarray morphology was demonstrated by correlating the variation of surface area to the reactivity. The incorporation of cobalt ions was found to increase the specific surface area and thus enhance C3H8 conversion of CuMn2O4. The CuMn2O4/MnO2 nanoarray-based monoliths are promising types of emission control devices.

Graphical abstract: Copper manganese oxide enhanced nanoarray-based monolithic catalysts for hydrocarbon oxidation

Back to tab navigation

Supplementary files

Publication details

The article was received on 05 Jul 2018, accepted on 13 Sep 2018 and first published on 18 Sep 2018


Article type: Paper
DOI: 10.1039/C8TA06459H
Citation: J. Mater. Chem. A, 2018,6, 19047-19057

  •   Request permissions

    Copper manganese oxide enhanced nanoarray-based monolithic catalysts for hydrocarbon oxidation

    S. Chen, W. Tang, J. He, R. Miao, H. Lin, W. Song, S. Wang, P. Gao and Steven L. Suib, J. Mater. Chem. A, 2018, 6, 19047
    DOI: 10.1039/C8TA06459H

Search articles by author

Spotlight

Advertisements