Supercritical-fluid synthesis of FeF2 and CoF2 Li-ion conversion materials

Abstract

The synthesis of the Li-ion conversion candidates, FeF2 and CoF2, obtained from the single source organometallic precursors [Fe(tta)3] (tta = C8H4F3O2S), and [Co(hfac)2·2H2O] (hfac = C5H1F6O2), respectively, via a novel supercritical fluid (SCF) method is presented. The nature of the synthesis led to highly-crystalline FeF2 and CoF2 powders requiring no additional thermal treatment. The as-obtained powders were investigated for use as potential positive Li-ion conversion electrodes by means of chronopotentiometric measurements. The FeF2 cells displayed high initial capacities following electrochemical conversion (up to ∼1100 mA h g−1 at a potential of 1.0 V vs. Li/Li+), with appreciable cyclic behaviour over 25 discharge–charge cycles. The deposition of a ∼5 nm layer of amorphous carbon onto the surface of the active material following SCF treatment, likely facilitated adequate electron transport through an otherwise poorly conducting FeF2 phase. Similarly, CoF2 cells displayed high initial capacities (up to ∼650 mA h g−1 at a potential of 1.2 V vs. Li/Li+), although significant capacity fading ensued in the subsequent cycles. Ex situ XRD measurements confirmed a poor reversibility in the conversion sequence for CoF2, with a complete loss of CoF2 crystallinity and the sole presence of a crystalline LiF phase following charging.

Graphical abstract: Supercritical-fluid synthesis of FeF2 and CoF2 Li-ion conversion materials

Article information

Article type
Paper
Submitted
21 Jun 2013
Accepted
22 Jul 2013
First published
23 Jul 2013

J. Mater. Chem. A, 2013,1, 10667-10676

Supercritical-fluid synthesis of FeF2 and CoF2 Li-ion conversion materials

M. J. Armstrong, A. Panneerselvam, C. O'Regan, M. A. Morris and J. D. Holmes, J. Mater. Chem. A, 2013, 1, 10667 DOI: 10.1039/C3TA12436C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements