Unusual structural evolution of poly(lactic acid) upon annealing in the presence of an initially oriented mesophase

Abstract

Uniaxial deformations of amorphous poly(lactic acid) (PLA) films were performed at two different temperatures, 70 and 80 °C, at various draw strains. The samples deformed at 70 °C showed a strain-induced mesophase, and the structural ordering and thermal stability increased as the draw strain increased. Further annealing was performed in situ at constant length at the drawing temperature of 70 °C for the films drawn to strains of 100% and 230%. Unusually, we found that after annealing, the crystal structure of the film at lower strain was more ordered than the one at higher strain. Further investigations revealed that upon annealing the structural evolution followed a distinct molecular mechanism for the samples stretched to the two draw strains. For the sample drawn to 100%, the mesophase melted very quickly upon annealing, resulting in chain randomization and the release of the constraints on the thermodynamic relaxation of the oriented amorphous chains. The chain relaxation motions had a beneficial effect on the occurrence of the conformational rearrangements that are necessary for crystalline ordering. By contrast, for the 230% sample, the melting of the mesophase was slow and most of the chain orientations were preserved upon annealing. As a result, a less ordered crystal structure was formed since the local relaxation motions that are necessary for promoting crystalline order via conformational rearrangements were hindered.

Graphical abstract: Unusual structural evolution of poly(lactic acid) upon annealing in the presence of an initially oriented mesophase

Article information

Article type
Paper
Submitted
09 Oct 2013
Accepted
02 Dec 2013
First published
05 Dec 2013

Soft Matter, 2014,10, 1512-1518

Unusual structural evolution of poly(lactic acid) upon annealing in the presence of an initially oriented mesophase

Y. Wang, M. Li, K. Wang, C. Shao, Q. Li and C. Shen, Soft Matter, 2014, 10, 1512 DOI: 10.1039/C3SM52611A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements