Study of the hydrogen-induced amorphization in the LaNi2.28 alloy

Author affiliations

Abstract

To understand the fundamental reason leading to the poor stability of LaNi2.28 hydrogen storage alloy, the cycling behavior of LaNi2.28 alloy under hydrogen has been investigated. The present study describes the hydrogen-induced amorphization (HIA) of LaNi2.28 alloy. The phase composition, microstructure and morphology of the phases are observed and analyzed using X-ray diffraction and scanning electron microscopy. The crystal structure and chemical composition of the amorphized alloy show that HIA is found in the sample at different cycles of the hydrogenation process. During the first hydrogenation cycle, the degree of HIA is indeclinable with the increased cycle. In addition, the formation processes of amorphous alloys, the occurrence of HIA and the relationship between the structure of the hydrogen-induced amorphous alloy and the stability of LaNi2.28 are given. The conclusions can be summarized as follows: 2LaNi2.28 + H2 → LaNi2.28Hx (amorphous) + LaNi5Hy + LaH2, and amorphous LaNi2.28Hx and LaNi5Hy can desorb 50% hydrogen of the absorption capacity of LaNi2.28, and the absorption–desorption capacity is stable after the first cycle.

Graphical abstract: Study of the hydrogen-induced amorphization in the LaNi2.28 alloy

Back to tab navigation

Publication details

The article was received on 16 Mar 2014, accepted on 28 May 2014 and first published on 28 May 2014


Article type: Paper
DOI: 10.1039/C4RA02302A
Author version
available:
Download author version (PDF)
Citation: RSC Adv., 2014,4, 27207-27212

  •   Request permissions

    Study of the hydrogen-induced amorphization in the LaNi2.28 alloy

    P. Li, F. Zhai, Q. Wan, K. Zhao, Z. Li, A. A. Volinsky and X. Qu, RSC Adv., 2014, 4, 27207
    DOI: 10.1039/C4RA02302A

Search articles by author

Spotlight

Advertisements