Microwave selective heating-enhanced reaction rates for mullite preparation from kaolinite

Abstract

Mullite is becoming increasingly important for use in refractory lining, structural ceramic and catalyst products. The kaolinite-mullite process is a simple method to prepare mullite. Under conventional heating kaolinite has to be heated at 1400 °C for 1 h to form well-ordered orthorhombic mullite (3Al2O3·2SiO2) that is accompanied by the formation of cristobalite. However, under microwave heating at 900 °C for 5 min and 1200 °C for 1 min, respectively, kaolinite transformed to well-ordered orthorhombic mullite without the formation of cristobalite. The ultra-fast heating rate of microwaves, due to selective heating, accelerated the nucleation and growth of mullite grains and changed the mullitization route of kaolinite. Before mullitization, the capacity for microwave absorption of decomposed kaolinite is dependent on the amount of structural OH up to a temperature of 522 °C and is then dependent on the amount of metakaolinite, gamma alumina and amorphous silica that are present in the sample. The dielectric loss of pseudo-tetragonal mullite has the highest value of the dielectric losses for all of the phases that result from the kaolinite-mullite process.

Graphical abstract: Microwave selective heating-enhanced reaction rates for mullite preparation from kaolinite

Article information

Article type
Paper
Submitted
19 Jul 2013
Accepted
19 Nov 2013
First published
21 Nov 2013

RSC Adv., 2014,4, 2640-2647

Microwave selective heating-enhanced reaction rates for mullite preparation from kaolinite

Z. Zhang, X. Qiao and J. Yu, RSC Adv., 2014, 4, 2640 DOI: 10.1039/C3RA43767A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements