γ-Fe2O3–MWNT/poly(p-phenylenebenzobisoxazole) composites with excellent microwave absorption performance and thermal stability†
Abstract
Ferromagnetic γ-Fe2O3 nanoparticles were successfully loaded into multi-walled carbon nanotubes (MWNTs) as probed by transmission electron microscopy. Upon incorporation of the γ-Fe2O3–MWNTs into poly(p-phenylenebenzobisoxazole) (PBO), a conjugated polymer with high mechanical strength and outstanding thermal and oxidative stability, microwave absorbing materials were obtained. Attributed to the special structure of the γ-Fe2O3–MWNTs, synergistic effects on dielectric loss and magnetic loss, and a better matched characteristic impedance of the composites were achieved. The optimal minimum reflection loss reached −32.7 dB at 12.09 GHz on a composite containing 12 wt% γ-Fe2O3–MWNTs with a thickness of 2.7 mm, and the corresponding bandwidth below −5 dB was 6.2 GHz. This demonstrated its potential applications as a low-density microwave absorbing material operating under extreme environments.