Electron beam irradiation treatment of Ag/Bi2WO6/CdWO4 heterogeneous material with enhanced photocatalytic activity

Author affiliations

Abstract

An efficient ternary heterostructure material Ag/Bi2WO6/CdWO4 was prepared via a facile hydrothermal route. The in situ loading precisely regulated the distribution of silver nanoparticles on the heterojunction surface. Besides, electron beam irradiation was used for artificially creating interface defects in the material, so the specific surface area of the material was increased. The introduction of defects was conducive for the migration of catalytically active substances towards the surface of the material. Under visible light irradiation, the degradation efficiency of the heterostructure material was improved significantly. Within 20 min, the removal efficiency of the treated material for carmine could reach about 100% (50 mL, 50 mg L−1), while that for hexavalent chromium (Cr6+), it could reach about 100% (50 mL, 10 mg L−1) within 90 min. In addition, the results showed that 4% Ag load rate had the best improvement on the photocatalytic performance of the ternary heterostructure material, irrespective of the degradation process of carmine, Cr6+ or rhodamine B (RhB). Optimum amount of supported in situ nano-silver induced resonance of the plasma on the catalytic interface and synergized with Bi3+ to improve the catalytic efficiency. PL, DRS and XPS results proved that the ternary heterostructure could effectively inhibit the rapid recombination of electron hole pairs of Ag/Bi2WO6/CdWO4. As for the role of electron beam irradiation, it could improve the content of free hydroxyl groups on the material surface and enhance the catalytic capacity of the Ag/Bi2WO6/CdWO4 heterogeneous material. A feasible reaction pathway and photocatalytic mechanism for the degradation of carmine was investigated by gas chromatography-tandem mass spectrometry (GC-MS), and the main role of ˙OH in the catalytic process was obtained by using different scavengers.

Graphical abstract: Electron beam irradiation treatment of Ag/Bi2WO6/CdWO4 heterogeneous material with enhanced photocatalytic activity

Back to tab navigation

Article information


Submitted
21 May 2019
Accepted
23 Jul 2019
First published
24 Jul 2019

New J. Chem., 2019,43, 13764-13774
Article type
Paper

Electron beam irradiation treatment of Ag/Bi2WO6/CdWO4 heterogeneous material with enhanced photocatalytic activity

R. Sun, J. Wang, T. Yang, R. He, K. Xue, L. Wang, X. Yu, J. Wang, T. Yang and W. Wang, New J. Chem., 2019, 43, 13764
DOI: 10.1039/C9NJ02571E

Social activity

Search articles by author

Spotlight

Advertisements