Cu2Sb–Al2O3–C nanocomposite alloy anodes with exceptional cycle life for lithium ion batteries

Abstract

Cu2Sb–Al2O3–C nanocomposite alloy material has been synthesized via a mechanochemical reduction of Sb2O3 with Al and Cu metals in the presence of carbon (acetylene black). X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and scanning electron microscopy (SEM) reveal that these nanocomposites are composed of nanostructured Cu2Sb particles in an amorphous Al2O3 and conductive carbon matrix. The presence of Al2O3 in the nanocomposite drastically improves the cycle life of the Cu2Sb–C material and enables a remarkable capacity retention of 80% over 500 cycles (330 mAh/g) after the first cycle. With a tap density of ∼1.4 g cm−3, Cu2Sb–Al2O3–C offers significantly higher volumetric capacity than the commonly used graphite anode. A conductive Cu framework supports the electrochemically-active Sb and results in low impedance and good rate capability, while the matrix of ceramic oxide and conductive carbon reduce the agglomeration of the nanocrystalline Cu2Sb particles and buffer the volume expansion/contraction that occurs during cycling. TEM of the electrodes that were cycled between 1 and 500 cycles shows the evolution of the morphology of Cu2Sb particles in the presence and absence of Al2O3. Because the Cu2Sb–Al2O3–C nanocomposite electrodes can operate well above the potential where lithium plating occurs, it is viewed as a safer alternative to graphite anodes.

Graphical abstract: Cu2Sb–Al2O3–C nanocomposite alloy anodes with exceptional cycle life for lithium ion batteries

Article information

Article type
Paper
Submitted
21 Jul 2011
Accepted
07 Dec 2011
First published
09 Jan 2012

J. Mater. Chem., 2012,22, 3242-3248

Cu2Sb–Al2O3–C nanocomposite alloy anodes with exceptional cycle life for lithium ion batteries

D. Applestone, S. Yoon and A. Manthiram, J. Mater. Chem., 2012, 22, 3242 DOI: 10.1039/C2JM13479A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements