Effects of Al substitution on the spontaneous polarization and lattice dynamics of the PbTi1−xAlxO3
Abstract
Al-doped PbTiO3 solid solutions were synthesized by a solid state method. Since
Maintenance work is planned from 09:00 BST to 12:00 BST on Saturday 28th September 2024.
During this time the performance of our website may be affected - searches may run slowly, some pages may be temporarily unavailable, and you may be unable to access content. If this happens, please try refreshing your web browser or try waiting two to three minutes before trying again.
We apologise for any inconvenience this might cause and thank you for your patience.
* Corresponding authors
a
Department of Physical Chemistry, University of Science and Technology Beijing, Beijing, P. R. China
E-mail:
xing@ustb.edu.cn
Fax: 86 10 6233 2525
Tel: 86 10 62334200
b
Department of Materials Science and Engineering, the University of Texas at Dallas, Richardson, TX, USA
E-mail:
jinguo.wang@utdallas.edu, moonkim@utdallas.edu
Fax: 1 972 883 5725
c State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, P. R. China
Al-doped PbTiO3 solid solutions were synthesized by a solid state method. Since
C. Sun, J. Wang, P. Hu, M. J. Kim and X. Xing, Dalton Trans., 2010, 39, 5183 DOI: 10.1039/C000608D
To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.
If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.
If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.
Read more about how to correctly acknowledge RSC content.
Fetching data from CrossRef.
This may take some time to load.
Loading related content