Phase stability of intercalated V2O5 battery cathodes elucidated through the Goldschmidt tolerance factor

Abstract

Orthorhombic V₂O₅ is a promising Mg battery cathode material, and reversible intercalation in the layered α-phase has been claimed experimentally. However, these results, based on electrochemistry and XRD, are controversial. Previous computational studies have predicted high activation barriers (∼1 eV) for ionic migration in α-V₂O₅, although improved Mg²⁺ mobility is expected in the δ-phase. Here, hybrid-exchange density functional theory is used to discuss structure, stability and intercalation in the α and δ phases, beginning with a model system with MV₂O₅ stoichiometry, and varying ionic radius of the M cations. The relative stability of the two phases upon intercalation of M is rationalised through a tolerance factor-like behavioural trend, providing a framework for phase selection using intercalants of different ionic size. This tolerance factor behaviour is due to the presence of ferroelectrically distorted (2 × 2 × 2) perovskite blocks within the α-V₂O₅ structure. The δ-phase is found to undergo a barrierless phase change to α in fully charged (de-intercalated) Mg_xV₂O₅ (x = 0), indicating that stabilisation of δ-Mg_xV₂O₅ is required at low x if the δ phase is to be retained for higher Mg mobility. By employing dispersion interactions to accurately reproduce the interlayer distance, activation barriers for ion migration are found to be higher than reported in previous studies, clarifying questions regarding the extent of Mg intercalation that can be achieved experimentally. Interlayer ions are found to lower activation barriers for Mg²⁺ mobility by up to ∼330 meV in the α phase by expanding the interlayer space. The results address open questions about the electrochemical performance of orthorhombic V₂O₅ as Mg battery cathode material, and indicate atomic level mechanisms that activate ionic mobility in layered V₂O₅.