Homogenization Enabled Efficient Regeneration of Spent Ni-rich LiNixCoyMn1-x-yO2 cathodes

Abstract

High-Ni LiNixCoyMn1-x-yO2 (NCM) oxides with low Co content have emerged as promising candidates for next-generation cathodes due to their high energy density and acceptable manufacturing costs, making them widely adopted in electric mobility applications. However, their limited service life highlights an urgent need for efficient and economical recycling methods. Direct regeneration via relithiation has demonstrated effective for chemical restoration of degraded cathodes at low cost, but repairing high-Ni NCM cathodes remains challenging due to their degradation mechanisms of intergranular cracking and particle fragmentation. To overcome these challenges, we exploit the weakened interactions along grain boundaries in post-cycled NCM cathodes, achieving morphological reconstruction and size homogenization of degraded Ni-rich NCM through mild ball milling. The resulting NCM nanoparticles expose more facets for Li+ diffusion compared with polycrystalline particles, effectively shortening the diffusion pathways during subsequent relithiation process and enabling efficient regeneration under low temperatures and short processing durations. This work provides valuable insights into designing effective repairing strategies for mechanically degraded cathodes, advancing the applicability of direct regeneration techniques and fostering the sustainable development of Li-ion batteries.