Abstract

We investigated diffusion memristors in the structure of Ag/Ta2O5/HfO2/Pt, in which active Ag ions control active metal ion diffusion and mimic biological brain functions. The CMOS compatible high-k metal oxide could control an Ag electrode that was ionized by applying an appropriate voltage to form a conductive filament, and the movement of Ag ions was chemically and electrically controlled due to oxygen density. This diffusion memristor exhibited diffused characteristics with a selectivity of 109, and achieved a low power consumption of 2 mW at a SET voltage of 0.2 V. The threshold transitions were reliably repeatable over 20 cycles for compliance currents of 10−6 A, 10−4 A, and no compliance current, with the largest standard deviation value of SET variation being 0.028. Upon filament formation, Ag ions readily diffused into the interface of the Ta2O5 and HfO2 layer, which was verified by investigating the Ag atomic percentage using XPS and vertical EDX and by measuring the relaxation time of 0.8 ms. Verified volatile switching device demonstrated the biological synaptic properties of quantum conductance, short-term memory, and long-term memory due to controlling the Ag. Diffusion memristors using designed control and switching layers as following film density and oxygen vacancy have improved results as low-power devices and neuromorphic devices compared to other diffusion-based devices, and these properties can be used for various applications such as selectors, synapses, and neuromorphic devices.

Graphical abstract: Volatile threshold switching and synaptic properties controlled by Ag diffusion using Schottky defects

Supplementary files

Article information

Article type
Communication
Submitted
18 Dec 2023
Accepted
05 Mar 2024
First published
05 Mar 2024

Nanoscale Horiz., 2024,9, 853-862

Volatile threshold switching and synaptic properties controlled by Ag diffusion using Schottky defects

Y. Jeon, D. Akinwande and C. Choi, Nanoscale Horiz., 2024, 9, 853 DOI: 10.1039/D3NH00571B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements