Facile preparation of lignocellulosic xerogels by alkali freezing and ambient drying

Abstract

Recently, the ambient drying method for the preparation of xerogels has attracted great attention due to its low cost and high drying efficiency. However, the strong capillary forces existing during ambient drying cause severe shrinkage or even collapse of the aerogels (called xerogels). Although chemical cross-linking or displacement of water by organic solvents have been tried to solve the problem, extensive usage of chemicals and time-consuming displacement processes seem to be environmentally unfriendly and complex. Herein, we reported a green and efficient method for the preparation of a lignocellulosic xerogel. The xerogel was fabricated by alkali freezing of unbleached eucalyptus fibers followed by water washing and ambient drying. The alkali freezing promoted fiber swelling and enhanced the hydrogen bonds among the fibers, resulting in the gelation of lignocellulosic fibers. In particular, the residual lignin in the fibers reduced the capillary force during the drying process. The resulting lignocellulosic xerogel achieved a low shrinkage rate (27.50%), low density (0.039 g cm−3), high porosity (97.57%), and excellent mechanical strength (782.23 kPa) as well as environmental stability, and low thermal conductivity (44.76 mW m−1 K−1). Similarly structured xerogels could be generated using recycled NaOH solution. This technique was suitable for production using various kinds of plant fibers, which shows its great scalable production prospects.

Graphical abstract: Facile preparation of lignocellulosic xerogels by alkali freezing and ambient drying

Supplementary files

Article information

Article type
Paper
Submitted
17 Feb 2024
Accepted
15 Apr 2024
First published
19 Apr 2024

Green Chem., 2024,26, 6501-6510

Facile preparation of lignocellulosic xerogels by alkali freezing and ambient drying

Q. Huang, Z. Li, J. Hu, W. Wang and W. Li, Green Chem., 2024, 26, 6501 DOI: 10.1039/D4GC00825A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements