Intraparticle ripening to create hierarchically porous Ti-MOF single crystals for deep oxidative desulfurization

Abstract

The catalytic oxidative desulfurization (ODS) technique is able to remove sulfur compounds from fuels, conducive to achieving deep desulfurization for the good of the ecological environment. Ti-based metal–organic frameworks (Ti-MOFs) possessing good affinity to organic reactants and considerable numbers of Ti active sites are promising catalysts for ODS. However, current Ti-MOFs suffer from severe diffusion limitations caused by the size mismatch between sole micropores and bulky sulfur compounds, leading to poor ODS performance. Here, a facile method of intraparticle ripening without any additive is developed to obtain hierarchically meso–microporous Ti-MIL-125 single crystals (Meso-Ti-MIL-125) for the first time. Such Meso-Ti-MIL-125 shows a BET surface area of 1401 m² g⁻¹ and a mesoporous volume that is 1.7 times as high as that of the conventional Ti-MIL-125. Our novel Meso-Ti-MIL-125 exhibits excellent catalytic performance in the ODS of a series of bulky thiophenic sulfur compounds, completely removing benzothiophene (BT), dibenzothiophene (DBT), and 4,6-dimethyldibenzothiophene (DMDBT) from model fuels, which is, respectively, 2.4 times, 1.5 times, and 6.7 times higher than the removal achieved with conventional Ti-MIL-125. Such a facile synthetic strategy is envisioned to be applied in many kinds of crystalline materials, such as zeolites, for industrial production.