Capturing CO2 by ceria and ceria–zirconia nanomaterials of different origin

Abstract

Ceria and ceria–zirconia nanomaterials of different origin were studied in order to elucidate the role of their structural and textural characteristics in controlling the performance towards CO2 capture. Two commercial cerias and two home-prepared samples, CeO2 and CeO2–ZrO2 (75% CeO2) mixed oxide, were investigated. The samples were characterized by a number of analytical techniques including XRD, TEM, N2-adsorption, XPS, H2-TPR, Raman and FTIR spectroscopy. Static and dynamic CO2 adsorption experiments were applied to assess the CO2 capture performance. The type of surface species formed and their thermal stability were evaluated by in situ FTIR spectroscopy and CO2–TPD analysis. The two commercial ceria samples possessed similar structural and textural characteristics, formed the same types of carbonate-like surface species upon CO2 adsorption and, consequently, demonstrated almost identical CO2 capture performance under both static and dynamic conditions. The thermal stability of the adsorbed species increased in the order bidentate (B) carbonates, hydrogen carbonates (HC) and tridentate carbonates (T-III, T-II, T-I). Reduction of CeO2 increased the relative amount of the most strongly bonded T-I tridentate carbonates. Preadsorbed water led to hydroxylation and enhanced formation of hydrogen carbonates. Although the synthesized CeO2 sample had a higher surface area (by 30%) it showed a disadvantageous long mass transfer zone in the CO2-adsorption breakthrough curves. Because of its complex pore structure, this sample probably experiences severe intraparticle CO2 diffusion resistance. Having the same surface area as the synthesized CeO2, the mixed CeO2–ZrO2 oxide exhibited the highest CO2 capture capacity of 136 μmol g−1 under dynamic conditions. This was related to the highest concentration of CO2 adsorption sites (including defects) on this sample. The CeO2–ZrO2 system showed the lowest sensitivity to the presence of water vapor in the gas stream due to the lack of dissociative water adsorption on this material.

Graphical abstract: Capturing CO2 by ceria and ceria–zirconia nanomaterials of different origin

Supplementary files

Article information

Article type
Paper
Submitted
26 Feb 2023
Accepted
30 May 2023
First published
31 May 2023

Phys. Chem. Chem. Phys., 2023,25, 17154-17175

Capturing CO2 by ceria and ceria–zirconia nanomaterials of different origin

D. Panayotov, V. Zdravkova, O. Lagunov, S. Andonova, I. Spassova, D. Nihtianova, G. Atanasova, N. Drenchev, E. Ivanova, M. Mihaylov and K. Hadjiivanov, Phys. Chem. Chem. Phys., 2023, 25, 17154 DOI: 10.1039/D3CP00896G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements