Polybenzimidazole Co-polymers; Synthesis, Morphology and High Temperature Fuel Cell Membrane Properties

Abstract

Polybenzimidazole (PBI) random co-polymers containing alicyclic and aromatic backbones were synthesized by using two different dicarboxylic acids (viz., cyclohexane dicarboxylic acid and terephthalic acid) by varying their molar ratios. The synthesized co-polymers were characterized by inherent viscosity (IV), Fourier transform infrared spectroscopy (FTIR), 1H nuclear magnetic resonance (1H NMR), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The co-polymer composition was determined by 1H NMR spectroscopy. The cyclohexyl based PBI possessed proton conductivity lower (114 mS/cm) than terephthalic acid based PBI (220 mS/cm). The aromatic PBI has high tensile modulus of 11 GPa whereas modulus of cyclohexyl PBI is only 2 GPa. By suitably selecting the monomer concentration, co-polymer properties can be altered (both proton conductivity and mechanical property). Out of different co-polymers, one synthesized using 30 mol % cyclohexane dicarboxylic acid and 70 mol % terephthalic acid exhibited good elongation (8 %), modulus (10.5 GPa) and improved proton conductivity (242 mS/cm). In the doped condition, the co-polymer registered an elongation of 52 % and tensile modulus of 170 MPa. High conductivity of this composition is attributed to the presence of ordered domains (field emission scanning electron microscopy) present in the co-polymer in the doped condition. The co-polymers are thermally stable and thermal stability increased with increase in aromatic content. Thus alicyclic-aromatic copolymerization is a viable technique to prepare high temperature proton exchange membranes.

Back to tab navigation

Supplementary files

Publication details

The article was received on 17 Sep 2019, accepted on 30 Nov 2019 and first published on 02 Dec 2019


Article type: Paper
DOI: 10.1039/C9PY01403A
Polym. Chem., 2019, Accepted Manuscript

  •   Request permissions

    Polybenzimidazole Co-polymers; Synthesis, Morphology and High Temperature Fuel Cell Membrane Properties

    S. B. Kumar, B. Sana, G. Unnikrishnan, T. Jana and S. K. Shankar, Polym. Chem., 2019, Accepted Manuscript , DOI: 10.1039/C9PY01403A