A rechargeable aqueous Zn2+-battery with high power density and a long cycle-life

Author affiliations


Li-Ion batteries (LIBs) are approaching their energy limits imposed by their intercalation chemistry nature. As alternatives, multivalent (MV) chemistries bring both promises and challenges, with the main obstacle being the sluggish diffusion of MV-cations due to their strong electrostatic interaction with host lattices. In this work, we demonstrated that polyanion based robust crystal architecture could enable ultrafast and reversible Zn2+-intercalation and de-intercalation at a high working voltage. The nominal bivalence of Zn2+ was successfully delocalized by multiple atoms through the p–d hybridization between the V-d and O-p orbitals; hence the inserted Zn2+ only bears an effective charge of 1.336, rendering its high mobility. The novel aqueous rechargeable 1.7 V Zn/LiV2(PO4)3 cell based on such a mechanism delivers a high power density (8000 W kg−1 at 60C) comparable to supercapacitors, and a high energy density (218 W h kg−1 at 1C) close to LIBs, with an extraordinarily long cycle life of 4000 cycles. All of these parameters far exceed those of Zn batteries reported so far. The cell-level volumetric and specific energy densities of the Zn/LiV2(PO4)3 cell are 320 W h L−1 and 150 W h kg−1, respectively, which are even better than those of first-generation LIBs. Combined with the intrinsic safety of its aqueous chemistry and its wide working temperature range, this cell makes a strong candidate for automotive applications.

Graphical abstract: A rechargeable aqueous Zn2+-battery with high power density and a long cycle-life

Back to tab navigation

Supplementary files

Publication details

The article was received on 29 Jun 2018, accepted on 03 Oct 2018 and first published on 03 Oct 2018

Article type: Communication
DOI: 10.1039/C8EE01883A
Citation: Energy Environ. Sci., 2018,11, 3168-3175

  •   Request permissions

    A rechargeable aqueous Zn2+-battery with high power density and a long cycle-life

    F. Wang, E. Hu, W. Sun, T. Gao, X. Ji, X. Fan, F. Han, X. Yang, K. Xu and C. Wang, Energy Environ. Sci., 2018, 11, 3168
    DOI: 10.1039/C8EE01883A

Search articles by author