Structure and dynamics of high-temperature strontium aluminosilicate melts

Author affiliations


We report the study of high-temperature melts (1600–2300 °C) and related glasses in the SrO–Al2O3–SiO2 phase diagram considering three series: (i) depolymerized ([SrO]/[Al2O3] = 3); (ii) fully polymerized ([SrO]/[Al2O3] = 1); and (iii) per-aluminous ([SrO]/[Al2O3] < 1). By considering the results from high-temperature 27Al NMR and high-temperature neutron diffraction, we demonstrate that the structure of the polymerized melts is controlled by a close-to-random distribution of Al and Si in the tetrahedral sites, while the depolymerized melts show smaller rings with a possible loss of non-bridging oxygens on AlO4 units during cooling for high-silica compositions. A few five-fold coordinated VAl sites are present in all compositions, except per-aluminous ones where high amounts of high-coordinated aluminium are found in glasses and melts with complex temperature dependence. In high-temperature melts, strontium has a coordination number of 8 or less, i.e. less than in the corresponding glasses. The dynamics of high-temperature melts were studied from 27Al NMR relaxation and compared to macroscopic shear viscosity data. These methods provide correlation times in close agreement. At very high temperatures, the NMR correlation times can be related to the oxygen self-diffusion coefficient, and we show a decrease of the latter with increasing Si/(Al + Si) ratios for polymerized melts with no compositional dependence for depolymerized ones. The dominant parameter controlling the temperature dependence of the aluminum environment of all melts is the distribution of Al–(OSi)p(OAl)(4-p) units.

Graphical abstract: Structure and dynamics of high-temperature strontium aluminosilicate melts

Back to tab navigation

Supplementary files

Publication details

The article was received on 01 Aug 2018, accepted on 11 Oct 2018 and first published on 12 Oct 2018

Article type: Paper
DOI: 10.1039/C8CP04908D
Citation: Phys. Chem. Chem. Phys., 2018,20, 27865-27877

  •   Request permissions

    Structure and dynamics of high-temperature strontium aluminosilicate melts

    P. Florian, A. Novikov, J. W. E. Drewitt, L. Hennet, V. Sarou-Kanian, D. Massiot, H. E. Fischer and D. R. Neuville, Phys. Chem. Chem. Phys., 2018, 20, 27865
    DOI: 10.1039/C8CP04908D

Search articles by author