Microwave assisted synthesis, characterization and thermoelectric properties of nanocrystalline copper antimony selenide thin films

Abstract

In the present work, we have synthesized p-type copper antimony selenide (Cu3SbSe4) thin films in an aqueous alkaline medium using a microwave assisted synthesis technique. The deposited thin films were characterized by UV-Vis-NIR spectroscopy, X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDS), high-resolution transmission electron microscopy (HRTEM) and thermoelectric techniques. On the basis of experimental results, a possible reaction mechanism has been discussed in detail. The band gap of the as deposited film is 1.94 eV and after annealing it reaches 1.87 eV for Cu3SbSe4. XRD results indicate that the as deposited thin films of CuSbSe2 have an orthorhombic crystal structure with secondary mixed phases and after annealing this is converted to Cu3SbSe4 having a pure tetragonal crystal structure. FESEM micrographs of Cu3SbSe4 showed a spherically diffused granular morphology having an average grain size of 25 nm. The HRTEM result of Cu3SbSe4 shows good crystallinity with a lattice spacing of 0.327 nm along the (112) plane. The EDS spectrum shows the presence of Cu, Sb and Se elements. The thermoelectric figure of merit (ZT) of the as deposited film is calculated to be 0.059 at 300 K and that of annealed Cu3SbSe4 is found to be 0.141 at 300 K.

Graphical abstract: Microwave assisted synthesis, characterization and thermoelectric properties of nanocrystalline copper antimony selenide thin films

Supplementary files

Article information

Article type
Paper
Submitted
25 Jul 2014
Accepted
30 Sep 2014
First published
02 Oct 2014

RSC Adv., 2014,4, 51632-51639

Microwave assisted synthesis, characterization and thermoelectric properties of nanocrystalline copper antimony selenide thin films

V. B. Ghanwat, S. S. Mali, S. D. Kharade, N. B. Pawar, S. V. Patil, R. M. Mane, P. S. Patil, C. K. Hong and P. N. Bhosale, RSC Adv., 2014, 4, 51632 DOI: 10.1039/C4RA07609E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements