Modification of SBA-15 pore connectivity by high-temperature

Author affiliations

Abstract

Two-dimensional hexagonally ordered CMK-3 carbons were synthesized using SBA-15 templates calcined at a temperature of 1153 K, whereas a disordered carbon was obtained using SBA-15 calcined at 1243 K, demonstrating that the pores connecting ordered mesopores in SBA-15 silica persist up to ca. 1153 K, but are eliminated at temperatures close to 1243 K.

Back to tab navigation

Publication details

The article was received on 05 Dec 2000, accepted on 17 Jan 2001 and first published on 07 Feb 2001


Article type: Communication
DOI: 10.1039/B009762O
Chem. Commun., 2001, 349-350

  •   Request permissions

    Modification of SBA-15 pore connectivity by high-temperature calcination investigated by carbon inverse replication

    H. J. Shin, R. Ryoo, M. Kruk and M. Jaroniec, Chem. Commun., 2001, 349
    DOI: 10.1039/B009762O

Search articles by author

Spotlight

Advertisements