A Y-doped P2-Na0.6Li0.11Fe0.27Mn0.62O2 cathode with improved high-rate capability and cycling stability for Na-ion batteries

Abstract

P2-Na0.6Li0.11Fe0.27−xMn0.62YxO2 (x = 0, 0.5%, 1%, and 2%) cathode materials were successfully prepared using a traditional solid-state method with ball milling-assisted modification. The effect of Y-doping on the crystal structure, grain size, morphology and sodium storage performance of Na0.6Li0.11Fe0.27Mn0.62O2 was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), galvanostatic charge–discharge cycling tests, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The results demonstrated that the ball-milling pre-treatment method could effectively reduce the grain size and mitigate the aggregation of Na0.6Li0.11Fe0.27Mn0.62O2. Additionally, reasonable Y-doping (x = 1%) significantly enhances the rate capability and cycling stability of Na0.6Li0.11Fe0.27Mn0.62O2via improving the Na+ diffusion kinetics and the reversibility of the oxygen redox reaction. These results indicate that Na0.6Li0.11Fe0.26Mn0.62Y0.01O2 is a promising candidate material for high-rate and long-life cathodes for Na-ion battery application.

Graphical abstract: A Y-doped P2-Na0.6Li0.11Fe0.27Mn0.62O2 cathode with improved high-rate capability and cycling stability for Na-ion batteries

Supplementary files

Article information

Article type
Paper
Submitted
29 Apr 2023
Accepted
30 Mai 2023
First published
31 Mai 2023

New J. Chem., 2023,47, 12109-12116

A Y-doped P2-Na0.6Li0.11Fe0.27Mn0.62O2 cathode with improved high-rate capability and cycling stability for Na-ion batteries

M. Cao, R. Li, F. Huang, X. Cai, M. Cui, S. Lin, J. Tian, Y. Jiang, Z. Shadike and Z. Fu, New J. Chem., 2023, 47, 12109 DOI: 10.1039/D3NJ01980B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements