Abstract

Crystallites of the W-type hexaferrites, Sr(Ni1−xZnx)2Fe16O27 (x = 0, 0.5, 1) have been aligned without applying magnetic field nor hot compaction, but through a simple synthesis process taking advantage of easy alignment of non-magnetic interacting, anisotropic-shaped precursor crystallites of goethite. The goethite precursor was prepared through a simple hydrothermal synthesis route, forming lathlike crystallites with apparent dimensions of 23.3 × 40.1 × 11.0 nm3 as extracted from powder X-ray diffraction along the a-, b- and c-axis, respectively. The calcined pellets consisted of almost phase pure W-type hexaferrites with relative small impurities of spinel ferrite (≤9.02(3) wt%). The high synthesis temperature resulted in large crystallites, which in turn caused low coercivities (Hc ≤ 5.4(1) kA m−1) and a squareness ration (Mr/Ms, remanence (Mr) over saturation magnetisation (Ms)) close to zero for all samples. The vanishing coercivity makes Mr/Ms an unsatisfying measure of preferred orientation. Quantitative texture analysis of the samples was carried out based on 2D transmission synchrotron diffraction data collected at different orientations of the samples. The texture investigations revealed alignment of the crystallites with the c-axis normal to the pressing surface of the pellets. The SrNi2Fe16O27 sample showed the highest texture index of 7.5 m.r.d.2.

Graphical abstract: Texture formation in W-type hexaferrite by cold compaction of non-magnetic interacting anisotropic shaped precursor crystallites

Article information

Article type
Paper
Submitted
30 Jun 2022
Accepted
01 Dez 2022
First published
08 Dez 2022

Dalton Trans., 2023,52, 281-289

Texture formation in W-type hexaferrite by cold compaction of non-magnetic interacting anisotropic shaped precursor crystallites

C. G. Knudsen, M. I. Mørch and M. Christensen, Dalton Trans., 2023, 52, 281 DOI: 10.1039/D2DT02091B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements