Operando video microscopy of Li plating and re-intercalation on graphite anodes during fast charging

Abstract

Despite the demand for fast-charging lithium (Li)-ion batteries, high-energy-density batteries with thick graphite anodes are limited by Li plating when charging at >4C rates. In this work, plan-view operando video microscopy is applied on >3 mA h cm−2 calendared graphite electrodes to study the dynamic evolution of local state-of-charge (SoC) and Li plating during fast charging. This technique allows for visualization of the spatial heterogeneity in SoC across the electrode, nucleation and growth of Li filaments, Li re-intercalation into graphite, “dead Li” formation, and SoC equilibration. The operando microscopy analysis is complemented by ex situ imaging of through-plane gradients in SoC to gain a three-dimensional visualization of spatial heterogeneity. We demonstrate that (1) Li plating preferentially nucleates on the graphite particles that lithiate fastest during fast charging; (2) the onset of Li plating correlates with the local minimum of the graphite electrode potential; (3) galvanic corrosion currents are responsible for Li re-intercalation, dead Li formation, and SoC re-equilibration after fast charging; and (4) electrochemical signatures during OCV rest or discharge are associated with Li re-intercalation into graphite. This work provides insight into the Li–graphite interactions at the composite electrode level and can be used to inform strategies to diagnose and mitigate Li plating during fast charging.

Graphical abstract: Operando video microscopy of Li plating and re-intercalation on graphite anodes during fast charging

Supplementary files

Article information

Article type
Paper
Submitted
16 Jul 2021
Accepted
05 Okt 2021
First published
18 Okt 2021

J. Mater. Chem. A, 2021,9, 23522-23536

Author version available

Operando video microscopy of Li plating and re-intercalation on graphite anodes during fast charging

Y. Chen, K. Chen, A. J. Sanchez, E. Kazyak, V. Goel, Y. Gorlin, J. Christensen, K. Thornton and N. P. Dasgupta, J. Mater. Chem. A, 2021, 9, 23522 DOI: 10.1039/D1TA06023F

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements