Preparation of yolk–shell urchin-like porous Co3O4/NiO@C microspheres with excellent lithium storage performance

Abstract

Yolk–shell urchin-like porous Co3O4/NiO@C microspheres were successfully synthesized via a facile solvothermal method and annealing treatment under an argon atmosphere. High reversible specific capacity, long cycling stability, and excellent rate capability were achieved for the material due to its specific yolk–shell urchin-like porous structure and coated carbon layers. The pores distributed on the yolk and shell, as well as the gap between the yolk and shell, provide numerous pathways for the penetration of electrolyte, and enhance the reversible specific capacity (the initial discharge specific capacity was as high as 1405.7 mA h g−1 at 0.1 C). Meanwhile, the stress and volume expansion could be greatly released and relieved through the pores, and long cycling stability was achieved (a high reversible specific capacity of 502.7 mA h g−1 was maintained after 1000 cycles at 5 C). The coated carbon layers greatly enhance the conductivity of the yolk–shell urchin-like porous Co3O4/NiO microspheres, accelerate the transmission of electrons, and improve their rate performance (a reversible specific capacity of 397.5 mA h g−1 was achieved when the current density was increased to 10 C).

Keywords: Yolk–shell; Urchin-like; Co3O4/NiO@C microspheres; Anode; Lithium storage.

Graphical abstract: Preparation of yolk–shell urchin-like porous Co3O4/NiO@C microspheres with excellent lithium storage performance

Supplementary files

Article information

Article type
Paper
Submitted
21 Aug 2022
Accepted
26 Okt 2022
First published
17 Nov 2022
This article is Open Access
Creative Commons BY-NC license

Ind. Chem. Mater., 2023,1, 247-253

Preparation of yolk–shell urchin-like porous Co3O4/NiO@C microspheres with excellent lithium storage performance

L. Yu, Q. Yang, G. Zhu and R. Che, Ind. Chem. Mater., 2023, 1, 247 DOI: 10.1039/D2IM00017B

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements