An in situ XAS study of high surface-area IrO2 produced by the polymeric precursor synthesis

Abstract

Iridium oxide powders with a surface area of more than 1 m2 g−1 (4 m2 g−2 from the H-UPD charge) and iridium-oxide crystallites less than 10 nm across were synthesized by heat treating gels formed from citric acid, ethylene glycol and dihydrogen hexachloroiridate(IV) in air. The characteristics of the resulting material was found to be strongly dependent on the heat-treatment step in the synthesis. A single heat-treatment of the gel resulted in a material with a substantial fraction of elemental iridium metal, i.e. iridium in oxidation state zero (Ir0). Post-synthesis modification of the powder by potential cycling resulted in oxidation peaks consistent with the conversion of the metal phase to iridium oxide. Linear combination of the near-edge part of the X-ray absorption data (X-ray absorption near-edge spectroscopy, XANES) collected in situ during potential cycling and an analysis of the extended X-ray fine-structure (EXAFS) part of the spectrum showed that the overall metal fraction was not significantly affected by the cycling. The oxidation of the metal phase is therefore limited to a thin layer of oxide at the metal surface, and a significant part of the iridium is left inactive. A modification of the heat treatment procedure of the sample resulted in iridium oxide containing only insignificant amounts of elemental iridium metal.

Graphical abstract: An in situ XAS study of high surface-area IrO2 produced by the polymeric precursor synthesis

Supplementary files

Article information

Article type
Paper
Submitted
14 Jan 2020
Accepted
27 Mär 2020
First published
30 Mär 2020

Phys. Chem. Chem. Phys., 2020,22, 18868-18881

An in situ XAS study of high surface-area IrO2 produced by the polymeric precursor synthesis

A. H. Reksten, A. E. Russell, P. W. Richardson, S. J. Thompson, K. Mathisen, F. Seland and S. Sunde, Phys. Chem. Chem. Phys., 2020, 22, 18868 DOI: 10.1039/D0CP00217H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements