On the nature of niobium substitution in niobium doped titania thin films by AACVD and its impact on electrical and optical properties

Abstract

Niobium doped TiO2 thin films were deposited on silica coated glass substrate using aerosol assisted chemical vapour deposition (AACVD) from hexane solution, at 500 °C. The as-deposited films appeared blue, were transparent in the visible, were reflective in the IR region at around 30% and were electrically conductive (n = 1.23 × 1019 cm−3, μ = 18.9 cm2 V−1 s−1, sheet resistance = 120 Ω □−1). The structure of the films was investigated using XRD, Raman spectroscopy, XPS and X-ray absorption spectroscopy (XAS). No visible phase segregation was found by XRD nor by Raman, though analysis of the Nb K-edge using XANES and EXAFS revealed the presence of niobium both incorporated into the titanium dioxide lattice as well as present in the form of Nb2O5. The high resolution TEM imaging showed sub 4 nm Nb2O5 crystals within the lattice. This work questions the solubility limit of niobium in the TiO2 lattice and suggests previous literature on Nb-doped TiO2 may have overestimated the degree of niobium substitution.

Graphical abstract: On the nature of niobium substitution in niobium doped titania thin films by AACVD and its impact on electrical and optical properties

Supplementary files

Article information

Article type
Paper
Submitted
25 Mai 2015
Accepted
23 Jul 2015
First published
28 Jul 2015

J. Mater. Chem. A, 2015,3, 17755-17762

Author version available

On the nature of niobium substitution in niobium doped titania thin films by AACVD and its impact on electrical and optical properties

A. J. Gardecka, G. K. L. Goh, G. Sankar and I. P. Parkin, J. Mater. Chem. A, 2015, 3, 17755 DOI: 10.1039/C5TA03772G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements