Enhancing the thermoelectric performance of Cu1.8S by Sb/Sn co-doping and incorporating multiscale defects to scatter heat-carrying phonons

Abstract

Cu-based chalcogenides have attracted increasing attention as a potential thermoelectric material due to their unique structural features, high element abundance, and low toxicity. In this paper, a series of Cu1.8SbxSnyS compositions (0.01 < x < 0.04, 0.015 < y < 0.045) were prepared by a simple method combining mechanical alloying (MA) and spark plasma sintering (SPS). The results demonstrate that Sb/Sn co-doping can optimize the hole concentration and substantially improve the dimensionless figure of merit (ZT) of copper–sulfide Cu1.8S. The highest ZT, up to 1.2 at 773 K, was realized for the Cu1.8Sb0.02Sn0.03S sample and maintained a high power factor of 975 μW m−1 K−2. The reduction in thermal conductivity was linked to the heterogeneous phase of Cu12Sb4S13 and Cu4SnS4. Remarkably, after four testing cycles, the variation in ZT was less than 2%, indicating a good stability of the Sb/Sn co-doped Cu1.8S materials.

Graphical abstract: Enhancing the thermoelectric performance of Cu1.8S by Sb/Sn co-doping and incorporating multiscale defects to scatter heat-carrying phonons

Supplementary files

Article information

Article type
Communication
Submitted
26 Feb 2019
Accepted
14 Mär 2019
First published
14 Mär 2019

J. Mater. Chem. C, 2019,7, 4026-4031

Enhancing the thermoelectric performance of Cu1.8S by Sb/Sn co-doping and incorporating multiscale defects to scatter heat-carrying phonons

H. Tang, H. Zhuang, B. Cai, Asfandiyar, J. Dong, F. Sun and J. Li, J. Mater. Chem. C, 2019, 7, 4026 DOI: 10.1039/C9TC01096C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements