Abstract

Mixed powders of Bi2O3 and Fe2O3 are shown to yield single-phase, dense nanostructured polycrystals of BiFeO3 in reaction flash sintering experiments, carried out by applying a field of 50 V cm−1 and with the current limit set to 35 mA mm−2. The furnace was heated at a constant rate with the reaction sintering taking place abruptly upon reaching 625 °C. Remarkably, an intermediate bismuth-rich phase of the oxide that forms just before reaching the flash temperature transforms, and at the same time sinters, into single-phase BiFeO3 within a few seconds after the onset of the flash. The BiFeO3 so produced is electrically insulating, a property that is critical to its applications. This one-step synthesis of single-phase polycrystals of complex oxides from their basic constituents, by reaction flash sintering, is a significant development in the processing of complex oxides, which are normally difficult to sinter by conventional methods.

Graphical abstract: Phase-pure BiFeO3 produced by reaction flash-sintering of Bi2O3 and Fe2O3

Supplementary files

Article information

Article type
Paper
Submitted
20 Okt 2017
Accepted
22 Dez 2017
First published
22 Dez 2017

J. Mater. Chem. A, 2018,6, 5356-5366

Phase-pure BiFeO3 produced by reaction flash-sintering of Bi2O3 and Fe2O3

E. Gil-González, A. Perejón, P. E. Sánchez-Jiménez, M. J. Sayagués, R. Raj and L. A. Pérez-Maqueda, J. Mater. Chem. A, 2018, 6, 5356 DOI: 10.1039/C7TA09239C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements