In vitro degradation behavior of a hydroxyapatite/poly(lactide-co-glycolide) composite reinforced by micro/nano-hybrid poly(glycolide) fibers for bone repair

Abstract

A poly(glycolide) (PGA) fiber-reinforced hydroxyapatite/poly(lactide-co-glycolide) (HA/PLGA) composite with high mechanical strength has been prepared previously. In this paper, in vitro degradation of ternary composites with different contents of PGA fibers (0, 30, 50 and 70 wt%) was investigated. Water absorption showed a marked increase as the degradation progressed, and the composite with 70 wt% PGA fibers showed the highest final water uptake which was 3.89 times higher than the initial value. The mass loss of the composite with 70 wt% PGA fibers was 79.3 ± 6.47% at 16 weeks, which was the highest among all the composites. The molecular weight of the PLGA matrix decreased over time especially for the composites containing 70 wt% PGA fibers. The lowest pH of the buffer solution was also observed in the composite with 70 wt% PGA fibers. Environmental scanning electron microscopy (ESEM) and micro-computed tomography (micro-CT) results demonstrated that the porosity of the composites and the size of the pores gradually increased as the degradation progressed. The most significant change in compression strength was observed for the composite with 70 wt% PGA fibers which was reduced from an initial value of 20 MPa to approximately 1 MPa at 16 weeks. The results indicated that the in vitro degradation of the composites could be accelerated by increasing the content of PGA fibers. It implied that the ternary composites might be a candidate for the repair of non-load bearing or cancellous bone which needs high initial strength and fast degradation rate.

Graphical abstract: In vitro degradation behavior of a hydroxyapatite/poly(lactide-co-glycolide) composite reinforced by micro/nano-hybrid poly(glycolide) fibers for bone repair

Article information

Article type
Paper
Submitted
04 sep 2017
Accepted
11 okt 2017
First published
11 okt 2017

J. Mater. Chem. B, 2017,5, 8695-8706

In vitro degradation behavior of a hydroxyapatite/poly(lactide-co-glycolide) composite reinforced by micro/nano-hybrid poly(glycolide) fibers for bone repair

Y. Zhu, Z. Wang, L. Li, D. Gao, Q. Xu, Q. Zhu and P. Zhang, J. Mater. Chem. B, 2017, 5, 8695 DOI: 10.1039/C7TB02364B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements