MOF–polymer enhanced compatibility: post-annealed zeolite imidazolate framework membranes inside polyimide hollow fibers

Abstract

Thermal annealing, a commonly used procedure for improving the performance of polymeric membranes, is in this work exploited in the presence of a metal–organic framework (MOF) supported layer. MOFs and polymers are materials with a common organic character, suggesting an enhanced affinity between them when used together in membrane separation. Zeolite-like imidazolate frameworks (ZIFs) ZIF-8 and ZIF-93 with sod and rho structures and pore apertures of 0.34 and 0.36 nm, respectively, have been grown inside 356 μm OD co-polyimide P84 hollow fibers by microfluidics, leading to continuous supported membranes. When these membranes were thermally in situ annealed below the glass transition temperature, while monitoring both H2 and CH4 permeances, the MOF–polymer adhesion was enhanced. Thus the gas separation selectivity increased without any significant reduction in the gas permeance, and H2/CH4 and CO2/CH4 maximum selectivities of 103 and 18 (ZIF-8) and 101 and 20 (ZIF-93) were respectively measured. The good compatibility between MOF and polymer made improvements possible in the annealing of the membrane once it was prepared. If the annealing of the polymer was carried out before the MOF synthesis, the polymer chain rearrangement and surface smoothing prevented an optimum MOF–polymer interaction and the separation performance worsened. These results proved the compatibility between both materials and their synergistic contribution to gas selective transport.

Graphical abstract: MOF–polymer enhanced compatibility: post-annealed zeolite imidazolate framework membranes inside polyimide hollow fibers

Supplementary files

Article information

Article type
Paper
Submitted
07 dec 2015
Accepted
29 dec 2015
First published
06 jan 2016

RSC Adv., 2016,6, 5881-5889

MOF–polymer enhanced compatibility: post-annealed zeolite imidazolate framework membranes inside polyimide hollow fibers

F. Cacho-Bailo, G. Caro, M. Etxeberría-Benavides, O. Karvan, C. Téllez and J. Coronas, RSC Adv., 2016, 6, 5881 DOI: 10.1039/C5RA26076K

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements