Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

Development of active and intelligent films based on cassava starch and Chinese bayberry (Myrica rubra Sieb. et Zucc.) anthocyanins

Dawei Yun a, Huahao Cai a, Yunpeng Liu a, Lixia Xiao a, Jiangfeng Song *b and Jun Liu *a
aCollege of Food Science and Engineering, Yangzhou University, Yangzhou 225127, PR China. E-mail: junliu@yzu.edu.cn
bInstitute of Farm Product Processing, Jiangsu Academy of Agricultural Sciences, Nanjing 210014, PR China. E-mail: songjiangfeng102@163.com

Received 22nd August 2019 , Accepted 24th September 2019

First published on 30th September 2019


Abstract

Chinese bayberry (Myrica rubra Sieb. et Zucc.) fruit is a functional food rich in anthocyanins. In this study, anthocyanin-rich bayberry extract (BBE) was added into cassava starch to develop food packaging films with antioxidant and pH-sensitive properties. Results showed the main anthocyanin in BBE was cyanidin-3-O-glucoside (95.6%). The addition of 1 wt% of BBE into the film matrix resulted in a dense and compact internal microstructure, which greatly improved the water vapor permeability and tensile strength of the film. However, the addition of 2, 3 and 4 wt% of BBE into film matrix produced heterogeneous inner microstructures due to the formation of agglomerated BBE. The intermolecular interactions between BBE and the starch film matrix were through hydrogen binding. As compared with the starch film, starch–BBE films exhibited higher thicknesses, tensile strength, UV-vis light barrier and antioxidant properties. Moreover, starch–BBE films presented significant color changes when exposed to hydrogen chloride and ammonia gases. The pH-sensitive starch–BBE films were able to monitor the freshness of pork. Our results suggested that starch–BBE films could be used as smart and active packaging materials in the food industry.


1. Introduction

Due to the awareness of environmental problems caused by plastic packaging materials, researchers have paid increasing attention to the development of biodegradable packaging films.1 Many naturally originating biopolymers including polysaccharides, proteins and lipids have been applied to prepare biodegradable packaging films.2 Among several biopolymers, starch is often selected to develop packaging films because it is abundant, cheap, edible and biodegradable.3 In general, the physicochemical and functional properties of starch-based films are closely related to its source (e.g. corn, wheat, rice, potato and cassava).4,5 Cassava starch is regarded as a promising film-forming material because it has a low temperature of gelatinization and good gel stability.6 However, plain cassava starch films also have many drawbacks, such as lower mechanical, barrier and antioxidant properties.7 Therefore, many different natural ingredients including plant extracts, essential oils and other biopolymers have been incorporated into cassava starch films to improve the physical and functional properties of the films.8–10

Anthocyanins are the most important pigments of vascular plants and are responsible for the pink, red, violet and blue colors of vegetables and fruits.11 Anthocyanins are glycosides and acylglycoside derivatives of six common anthocyanidins: cyanidin, delphinidin, malvidin, pelargonidin, peonidin and petunidin, which are classified according to the number and position of hydroxyl groups on the flavan nucleus.12 Notably, anthocyanins present different chemical forms and colors as the function of pH.13 Thus, anthocyanin-rich films are considered as promising intelligent pH indicators to monitor the freshness of food since the process of food spoilage is usually accompanied by pH changes.14 Meanwhile, anthocyanins are one type of phenolic compounds with antioxidant and antibacterial activity, and are suitable to be incorporated into films to develop active packaging.15 Up to now, several intelligent and active packaging films have been developed by incorporating anthocyanins from different sources (e.g. blueberry, grape and Lycium ruthenicum) into cassava starch.6,16–21 The physical and functional properties of anthocyanin-rich films are generally affected by the source and content of anthocyanins.

Bayberry (Myrica rubra Sieb. et Zucc.) belongs to the family of Myricaceae, which is widespread in tropical, subtropical and temperate areas of the world.22 China is the major commercial production area for bayberry.23 Chinese bayberries contain several kinds of nutritional components, such as carbohydrates, sugars, organic acids, proteins, minerals, vitamins and phenolic compounds.24 Among different components, phenolic compounds from Chinese bayberries including phenolic acids, anthocyanins and flavonols have been demonstrated to possess potent antioxidant activity.25–27 In addition, the major anthocyanin present in Chinese bayberries is identified as cyanidin-3-O-glucoside, which represents more than 95% of the total pigment content.28 Therefore, it is supposed that anthocyanins from Chinese bayberries are suitable to be used to develop active and intelligent packaging.

In this study, we aimed at developing active and intelligent packaging by adding anthocyanin-rich Chinese bayberry extract (BBE) into cassava starch for the first time. The effects of BBE content on the structural, physical, antioxidant and pH-sensitive properties of starch-based films were determined. The developed films were also applied to monitor the freshness of pork.

2. Materials and methods

2.1. Materials and chemical reagents

Chinese bayberries (M. rubra) were purchased from the local market (Yangzhou, China). AB-8 macroporous resin was purchased from Bohong Resin Technology Co., Ltd. (Tianjin, China). Cassava starch was obtained from Ganzhiyuan Sugar Industry Co., Ltd. (Nanjing, China). 2,2-Diphenyl-1-picrylhydrazyl (DPPH) was purchased from Sigma Chemical Co. (MO, USA). Ethanol, glycerol, hydrochloric acid and ammonia were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). All other reagents were of analytical grade.

2.2. Extraction of anthocyanins

Anthocyanins were extracted from Chinese bayberries according to the method of Qin et al.20 with some modifications. The fresh bayberries (250 g) were ground and extracted twice in 1000 mL of 80% ethanol solution containing 0.5% HCl (v/v) at 4 °C for 24 h. All the extract solutions were combined and centrifuged at 8000g for 20 min to remove debris. The supernatant was further purified on the column of AB-8 macroporous resin (1.6 cm × 60 cm), which was continuously eluted with 80% ethanol solution containing 0.5% HCl (v/v). The collected eluate was concentrated by rotary evaporation at 40 °C, followed by vacuum drying to obtain BBE powder.

2.3. Characterization of anthocyanins

The anthocyanin content in BBE was measured by pH-differential assay.29 In addition, the composition of anthocyanins in the extract was further analyzed by Agilent 1200 HPLC system (Agilent Technologies, CA, USA) equipped with 6460 triple quadrupole mass spectrometer according to the chromatographic method of Zhang et al.30 The pH-sensitivity of BBE was analyzed by dissolving 2 mg BBE in 20 mL of different buffer solutions (pH 3–12) for 5 min, and the obtained BBE solutions were scanned on Lambda 35 ultraviolet-visible (UV-vis) spectrophotometer (PerkinElmer Inc., MA, USA) from 450 to 700 nm.

2.4. Development of the films

Starch films with and without BBE were developed by the method of Stoll et al.31 Briefly, 4% of starch solution was prepared by dissolving 6.8 g of starch in 170 mL of deionized water at 90 °C with continuous stirring. Afterwards, the starch solution was mixed with different contents of BBE (0, 1, 2, 3 and 4 wt%) and 25 wt% of glycerin based on the weight of starch. The resulting film-forming solutions were degassed, poured into Plexiglas plates (24 cm × 24 cm) and then dried in a ventilated climate chamber at 30 °C and 50% relative humidity for 48 h. The prepared films containing 0, 1, 2, 3 and 4 wt% of BBE were named as starch, starch–BBE I, starch–BBE II, starch–BBE III and starch–BBE IV films, respectively. All the films were stored at 20 °C and 50% relative humidity for at least 48 h before tests.

2.5. Structural characterization of the films

2.5.1. Scanning electron microscopy (SEM). The microstructure of the film was characterized by GeminiSEM 300 equipment (Carl Zeiss, Oberkochen, Germany). Film sample was fractured in liquid nitrogen, fixed on a stainless steel support with double-side conductive adhesive, sputtered with gold–palladium and analyzed on the SEM at 5 kV with the magnification of 400×.
2.5.2. Fourier transform infrared (FT-IR) spectroscopy. The FT-IR spectrum of the film was recorded on Varian 670 spectrometer (Varian Inc., CA, USA) in the wavenumber range of 4000–400 cm−1 with a total of 32 scans, operating at attenuated total reflection (ATR) mode.
2.5.3. X-ray diffraction (XRD). The crystalline character of the film was determined by D8 Advance X-ray diffractometer (Bruker AXS GmbH, Karlsruhe, Germany), conducting with Ni-filtered CuKα radiation at 40 mA and 40 kV. The XRD pattern was recorded from 2θ of 5–80° with the scanning rate of 0.2° s−1.

2.6. Determination of the physical properties of the films

2.6.1. Color. The color parameters (L, a and b) of the film were determined by SC-80C colorimeter (Kangguang Instrument Co. Ltd, China). The total color difference (ΔE) and whiteness index (WI) of the film were calculated by the following formulas:18
 
image file: c9ra06628d-t1.tif(1)
 
image file: c9ra06628d-t2.tif(2)
where L*, a* and b* were the color parameters of standard white plate used for calibration, and L, a and b were the color parameters of the film.
2.6.2. Thickness. The thickness of the film was determined by Mitutoyo no. 293-766 digital micrometer (Tester Sangyo Co., Ltd., Tokyo, Japan) through randomly selecting ten different positions on each film.
2.6.3. Water vapor permeability (WVP). The WVP of the film was determined by the method of Wang et al.32 Briefly, film sample (6 cm × 6 cm) was sealed over 50 mL of centrifuge tube containing 30 g of dried silica gel. The centrifuge tube was then maintained at 25 °C in a desiccator containing distilled water. The centrifuge tube was weighed every 24 h for 7 days. The WVP of the film was calculated as follows:
 
image file: c9ra06628d-t3.tif(3)
where W was the increased weight of the centrifuge tube (g), x was the film thickness (m), t was the time (s) for the weight gain of the centrifuge tube, A was the permeable area (m2) of water vapor, and ΔP was the saturated vapor pressure at 25 °C.
2.6.4. Light transmittance and opacity. The light transmittance of the film was measured by scanning film sample (4 cm × 0.9 cm) on Lambda 35 UV-vis spectrophotometer (PerkinElmer Ltd., MA, USA) at the wavelength range from 200 to 800 nm.
2.6.5. Mechanical properties. The mechanical properties of the film were determined by fixing the film strip (6 cm × 1 cm) on TMS-Pro Texture Analyzer (Food Technology Co., VA, USA) at a crosshead speed of 6 cm min−1.32 The tensile strength (TS) and elongation at break (EAB) of the film were calculated as follows:
 
image file: c9ra06628d-t4.tif(4)
 
image file: c9ra06628d-t5.tif(5)
where F was the stress for film fracture (N), x was film thickness (mm), W was film width (mm), ΔL was the increased length at film break (mm) and L0 was the initial film length (mm).
2.6.6. Thermogravimetric analysis (TGA). The thermal stability of the film was determined by heating film sample (2 mg) from 30 to 800 °C on Pyris 1 instrument (PerkinElmer Inc., MA, USA) under nitrogen atmosphere.

2.7. Determination of the antioxidant property of the films

The antioxidant property of the film was determined by DPPH radical scavenging test.33 Briefly, different amounts (4, 8, 12, 16 and 20 mg) of the film sample were weighed and individually placed in the test tubes. Then, 4 mL of 100 μM DPPH methanol solution was added into each tube and reacted with film sample at 25 °C for 1 h in the dark. The absorbance of the reaction solution was measured at 517 nm. The DPPH radical scavenging activity of the film was calculated as follows:
 
image file: c9ra06628d-t6.tif(6)
where A0 was absorbance of blank (without film) and A1 was absorbance of reaction solution containing film.

2.8. Determination of pH-sensitive property of the films

The pH sensitivity property of the film was determined by the method of Wu et al.34 with some modifications. Film samples (1.5 cm × 1.5 cm) were divided into two groups and placed in the headspace of the sealed containers loaded with 0.4 M hydrogen chloride and 0.4 M ammonia water, respectively. The color changes of the film sample were recorded every 5 min for 60 min. The color parameters of the film sample at different times were determined as described in Section 2.6.1.

2.9. Application of the films for monitoring the freshness of pork

The colorimetric films were applied to monitor the freshness of pork.20 Briefly, 30 g fresh pork was placed in a Petri dish and covered with polyethylene film. Film sample (2 cm × 2 cm) was fixed to the headspace of Petri dish. Then, the Petri dish was stored at 25 °C for 48 h. The color changes of film sample were recorded periodically. Meanwhile, the pH and total volatile basic nitrogen (TVB-N) values of the pork were determined based on the Chinese standards of GB 5009.237-2016 and GB 5009.228-2016, respectively.

2.10. Statistical analysis

Duncan test and one-way analysis of variance were carried out by SPSS 13.0 software package (SPSS Inc., IL, USA). Difference was considered as statistically significant if p < 0.05.

3. Results and discussion

3.1. Characterization of anthocyanins in BBE

Anthocyanins were extracted from Chinese bayberries and the total anthocyanin content in the extract was determined as 273 mg g−1 by pH-differential assay. The obtained extract was further separated by HPLC and identified by their mass spectra. As shown in Table 1, three kinds of anthocyanins including delphinidin-3-O-glucose (3.7%), cyanidin-3-O-glucoside (95.6%) and pelargonidin-3-O-glucose (0.7%) were detected, indicating cyanidin-3-O-glucoside was the main anthocyanin in BBE. This was consistent with the results of other researchers,22,35 who found cyanidin-3-O-glucoside was the primary anthocyanin in Chinese bayberry. Zhang et al.36 suggested the composition of anthocyanins was closely related with the cultivar of Chinese bayberries.
Table 1 The composition of anthocyanins in BBE as analyzed by HPLC-MS
Peak Retention time (min) Anthocyanins [M]+ (m/z) Relative content (%)
1 1.85 Delphinidin-3-O-glucose 465 3.7
2 5.92 Cyanidin-3-O-glucoside 449 95.6
3 7.56 Pelargonidin-3-O-glucose 433 0.7


3.2. Color variations of BBE in different buffer solutions

The color variations of BBE in different buffer solutions were shown in Fig. 1A. Significant color changes were observed in BBE solutions as the function of pH. When pH value was lower than 7, the color of BBE solution was red/pink. At the neutral condition (pH 7), a brown color was observed for BBE solution. However, the color of BBE solution turned purple at pH 8–10 and yellow at pH 11–12. Corresponding to the color variations of BBE in different buffer solutions, the maximum absorption peak of BBE solution gradually moved from 510 nm towards 590 nm with the increase of pH value (Fig. 1B). The color variations and corresponding bathochromic shift in the maximum absorption peak of BBE solution were caused by the structure transformation of anthocyanins at different pH conditions.37 Anthocyanins present the form of red flavylium cation in strong acidic conditions, which gradually transform into pink carbinol pseudobase, purple quinonoidal anhydrobase and finally light yellow chalcone in strong alkaline conditions.38 Similarly, other researchers also found anthocyanins from different sources (e.g. L. ruthenicum and purple sweet potato) exhibited color variations in different buffer solutions.14,20
image file: c9ra06628d-f1.tif
Fig. 1 Color variations (A) and UV-vis spectra (B) of BBE in different buffer solutions (pH 3 to 12).

3.3. Microstructure of starch–BBE films

The cross-sectional morphology of starch film and starch–BBE films is shown in Fig. 2. The cross-section of starch film was relatively smooth without significant wrinkles and protrusions, indicating that glycerol and starch were uniformly distributed in the film matrix. As compared to starch film, starch–BBE I film showed a more flat and dense cross-section. This suggested a low content (1 wt%) of BBE could be well mixed with other film components (e.g. starch and glycerol). The dense internal microstructure of starch–BBE I film was benefit to improve the water vapor barrier and mechanical properties of the film. However, starch–BBE II, III and IV films exhibited much rougher cross-sections as compared to starch and starch–BBE I films. The rougher cross-sections of starch films containing 2, 3 and 4 wt% of BBE were probably caused by the agglomerated BBE particles that occurred when the content of BBE exceeded 1 wt%. The heterogeneous inner microstructures of these films indicated the compactness of film network was destroyed by excessive extract. Similarly, Qin et al.20 found the cross-sectional morphology of starch-based films was closely related to the content of L. ruthenicum anthocyanins. The films presented dense inner microstructures when 1 and 2 wt% of anthocyanins was added, whereas the films exhibited a rough cross-section when 4 wt% of anthocyanins were incorporated. Zhang et al.39 also reported that starch–chitosan blend film containing 2.5 wt% of roselle anthocyanins had heterogeneous internal microstructures, revealing anthocyanins could destroy the ordered arrangement between starch and chitosan.
image file: c9ra06628d-f2.tif
Fig. 2 The cross-section morphology of starch (A), starch–BBE I (B), starch–BBE II (C), starch–BBE III (D) and starch–BBE IV (E) films.

3.4. FT-IR spectra of starch–BBE films

The intermolecular interactions between starch and BBE were revealed by ATR FT-IR technique and shown in Fig. 3. BBE presented characteristic bands of polyphenols at 3258 cm−1 (O–H stretching), 1604 cm−1 (C[double bond, length as m-dash]C stretching of aromatic ring) and 1015 cm−1 (C–H deformation of aromatic ring).40 Starch film exhibited bands at 3317 cm−1 (O–H stretching), 2926 cm−1 (C–H stretching of glucose residues), 1645 cm−1 (O–H bending of bound water), 994 to 1150 cm−1 (pyranose ring of glucose residues).41 The FT-IR spectra of starch–BBE films were somewhat different from that of starch film. On one hand, the O–H stretching of starch at 3317 cm−1 decreased and shifted to 3304 cm−1 after the incorporation of BBE, which was caused by the formation of hydrogen binding between BBE and starch that reduced the number of available hydroxyl groups. Similar results were also observed when anthocyanin-rich Jamaica flower extract was incorporated into starch based films.42 On the other hand, the O–H bending of bound water at 1645 cm−1 of starch slightly shifted to 1643/1642 cm−1 in starch–BBE films, suggesting the interactions (hydrogen binding) occurred between BBE and bound water. Choi et al.14 also observed that the band of potato starch/agar blend film at 1645 cm−1 shifted to a lower wavenumber (1617 cm−1) after the addition of anthocyanin-rich purple sweet potato extract, which was attributed to hydrogen binding between film matrix and the extract. Above results suggested that BBE was immobilized in the film matrix.
image file: c9ra06628d-f3.tif
Fig. 3 FT-IR spectra of BBE powder (a), and starch (b), starch–BBE I (c), starch–BBE II (d), starch–BBE III (e) and starch–BBE IV (f) films.

3.5. XRD patterns of starch–BBE films

The intermolecular interactions between BBE and starch can be also studied by XRD. As shown in Fig. 4, the XRD profile of BBE displayed a big broad peak at 2θ = 24°. This suggested BBE was in the amorphous state. Similar results were observed in other anthocyanin-rich plant extracts.20,40 As for starch film, it showed a broad peak at around 2θ = 20°. The formation of amorphous state in starch film was because the original semi-crystalline regions of starch granules were destroyed by heating during gelatinization.43 When BBE was added, the amorphous peak of starch film was almost unchanged. This indicated BBE was well dispersed in the film matrix. Notably, a new crystalline peak appeared at about 2θ = 24° when 2, 3 and 4 wt% of BBE were incorporated into starch film, which well corresponded to the amorphous peak position of BBE. The increased crystalline state in starch–BBE films was because of the formation of BBE agglomerates that exhibited the crystalline character. However, Zhai et al.43 reported that the incorporation of roselle anthocyanins decreased the crystalline state of starch/polyvinyl alcohol films, which could be explained by the hydrogen bonding formed between anthocyanins and film matrix. Qin et al.20 found the amorphous peak intensity of starch film increased after the addition of L. ruthenicum anthocyanins, which was probably because the hydrogen bonding formed between starch and anthocyanins resulted in three dimensional network. Above results suggested the crystallinity of anthocyanin-rich starch-based films were affected by the nature of anthocyanins.
image file: c9ra06628d-f4.tif
Fig. 4 XRD patterns of BBE powder (a), and starch (b), starch–BBE I (c), starch–BBE II (d), starch–BBE III (e) and starch–BBE IV (f) films.

3.6. Colors of starch–BBE films

Color is the most intuitive property of the film, which greatly affects the acceptance degree of consumers.44 As shown in Fig. 5A, the colors of starch–BBE films were significantly different from that of starch film. Starch film was colorless whereas starch–BBE films were purplish red. In addition, the colors of starch–BBE films deepened with the increase of BBE content. The purplish red colors of starch–BBE films were attributed to the presence of anthocyanins in BBE. The similar colors were observed in starch films containing L. ruthenicum anthocyanins.20Table 2 summarizes the color parameters of different films. Starch–BBE films showed higher a values than starch film, which was consistent with the red color of the films. The a values of starch–BBE films significantly increased when BBE content increased, which agreed with the gradually deepened color of starch–BBE films. In addition, the ΔE values of starch–BBE films significantly increased with the increase of BBE content, indicating starch–BBE films became more colored. However, the L and WI values of starch–BBE films decreased as BBE content increased, suggesting the tendency of the films toward dark. Above results indicated the color parameters of starch–BBE films were greatly affected by the content of the extract. Similar changes in the color parameters were obtained when anthocyanin-rich blackberry pulp and red rice flour were added into starch films.45,46
image file: c9ra06628d-f5.tif
Fig. 5 Physical appearances (A) and UV-vis light transmittance (B) of starch and starch–BBE films.
Table 2 Color values including L, a, b, ΔE and WI of starch and starch–BBE filmsa
Films L a b ΔE WI
a Values are given as mean ± SD (n = 3). Different letters in the same column indicate significantly different (p < 0.05).
Starch film 94.35 ± 0.05a −0.53 ± 0.01d −2.16 ± 0.06a 1.53 ± 0.04e 93.92 ± 0.07a
Starch–BBE I film 70.09 ± 0.83b 14.69 ± 0.66c −7.43 ± 0.21c 28.09 ± 1.08d 65.86 ± 1.06b
Starch–BBE II film 50.31 ± 0.71c 30.00 ± 0.47b −10.31 ± 0.10d 53.20 ± 0.85c 41.05 ± 0.85c
Starch–BBE III film 40.72 ± 1.56d 33.40 ± 0.23a −6.87 ± 1.13c 62.57 ± 1.09b 31.60 ± 1.13d
Starch–BBE IV film 36.84 ± 0.16e 32.96 ± 0.18a −4.10 ± 0.25b 66.59 ± 0.22a 28.64 ± 0.21e


3.7. Thicknesses of starch–BBE films

Film thickness is an important parameter that directly affects the mechanical strength, WVP and light transmittance of the film.47 As presented in Table 3, the thickness of starch and starch–BBE films varied from 0.076 to 0.089 mm. A significant enhancement in film thickness was observed when BBE content exceeded 1 wt%, which was because the high contents of the extract created heterogeneous film network that made the films became thicker. However, the incorporation of 1 wt% of BBE did not significantly change the thickness of the film. This result was in agreement the SEM observation that low content of BBE was well compatible with film matrix, which produced a dense internal microstructure. Qin et al.20 also found the thickness of anthocyanin-rich starch films was affected by the content of anthocyanins.
Table 3 Thicknesses, WVP, TS and EAB of starch and starch–BBE filmsa
Films Thickness (mm) WVP (×10−10 g m−1 s−1 Pa) TS (MPa) EAB (%)
a Values are given as mean ± SD (n = 10 for thickness, n = 3 for WVP, and n = 6 for TS and EAB). Different letters in the same column indicate significantly different (p < 0.05).
Starch film 0.076 ± 0.001b 1.084 ± 0.021c 8.41 ± 0.85d 4.26 ± 0.59a
Starch–BBE I film 0.078 ± 0.002b 0.984 ± 0.068d 11.74 ± 1.47a 4.19 ± 0.09a,b
Starch–BBE II film 0.089 ± 0.001a 1.112 ± 0.060b,c 11.16 ± 1.29a,b 4.01 ± 0.09a,b
Starch–BBE III film 0.087 ± 0.006a 1.164 ± 0.033b 10.47 ± 0.31b 3.83 ± 0.27b
Starch–BBE IV film 0.088 ± 0.001a 1.243 ± 0.051a 9.39 ± 0.20c 3.72 ± 0.14b


3.8. WVP of starch–BBE films

WVP is a vital barrier parameter for food packaging films to prevent moisture transfer between food and the environment. As shown in Table 3, the WVP value of starch–BBE I film (0.984 × 10−10 g m−1 s−1 Pa) was lower than that of starch film (1.084 × 10−10 g m−1 s−1 Pa), which was because the incorporation of a low content of BBE had created more dense and compact network to inhibit moisture transfer. In addition, the intermolecular interactions (i.e. hydrogen binding) between starch and BBE could reduced the availability of hydrophilic hydroxyl groups in starch–BBE films, thereby reducing the affinity of the films toward water vapor.20 However, the WVP values of starch–BBE films significantly increased when the content of BBE exceeded 2 wt%, which was because the excessive extract formed aggregates and produced more free volumes in the film network to facilitate moisture transfer. Luchese et al.6 found the incorporation of anthocyanin-rich blueberry residue significantly increased the WVP of starch film, which was due to the blueberry residue addition destructed the compactness of the film. Similarly, Nogueira et al.45 reported the addition 20, 30 and 40 wt% of blackberry pulp into starch films remarkably enhanced the WVP of the films, which was because blackberry pulp promoted the discontinuity of polymer matrix. Our results suggested the water vapor barrier property of starch film could be improved by incorporating 1 wt% of BBE.

3.9. Light transmittance of starch–BBE films

UV-vis light barrier property of the film is very important for light-sensitive food packaging. UV-vis light can accelerate food degradation and oxidation, leading to nutrient destruction, color loss and toxic substance formation.48 As shown in Fig. 5B, starch–BBE films showed significantly lower light transmittance in both UV and visible wavelength ranges as compared to starch film, suggesting starch–BBE films possessed higher UV-vis light barrier ability than starch film. The UV-vis light barrier ability of starch–BBE films was mainly attributed to the aromatic rings in the anthocyanins that could absorb UV-vis light.49 In addition, the UV-vis light barrier ability of starch–BBE films was positively correlated with BBE content in the films. Luchese et al.19 and Gutiérrez et al.50 also found the UV-vis light barrier property of anthocyanin-rich starch films was elevated with the increase of the content of anthocyanins. Notably, a significant reduction in the light transmittance at about 550 nm was observed for starch–BBE films, which corresponded to the visible absorption peak of anthocyanins. Similar phenomena were reported in starch films containing L. ruthenicum anthocyanins.20

3.10. Mechanical property of starch–BBE films

The mechanical properties including TS and EAB of different films are shown in Table 3. Starch–BBE films had relatively higher TS values (9.39–11.74 MPa) than starch film (8.41 MPa). The increased TS in starch–BBE films was because the abundant hydroxyl groups in anthocyanins could form hydrogen bonding with the hydroxyl groups in starch, resulting in stronger interfacial adhesion between starch and BBE.51 However, the TS of starch–BBE films gradually decreased as the BBE content increased, which was due to the excessive extract formed aggregates that interrupted the compactness of film network.43 The EAB values of starch–BBE I and II films (4.01–4.19%) were not significantly different from that of starch film (4.26%). Only starch–BBE III and IV films exhibited lower EAB values (3.72–3.83%) than starch film. This was probably because the BBE aggregates limited the motion of polymer chains, resulting in the decrease of film flexibility. The similar changes in the TS and EAB values were found when L. ruthenicum anthocyanins were added into starch films.20 Zhai et al.43 also reported the mechanical properties of starch/polyvinyl alcohol films were affected by the content of roselle anthocyanins. However, they found the TS values of the films decreased whereas the EAB values of the films increased with the increase of anthocyanin content. Therefore, the mechanical properties of anthocyanin-rich starch films could be related with the nature of anthocyanins.

3.11. Thermal property of starch–BBE films

The TGA and DTG profiles showed all the films were degraded in three stages (Fig. 6). For starch film, the first weight loss stage (30–185 °C) was associated with the release of free water in the film. The second weight loss stage (185–260 °C) was related to the evaporation of glycerol. The third weight loss stage (260–800 °C) was ascribed to the depolymerization and decomposition of starch molecules.52 However, the TGA and DTG profiles of starch–BBE films almost overlapped with those of starch film, indicating the incorporation of BBE did not significantly alter the thermal property of the films. Similarly, Qin et al.20 also reported the thermal property of starch-based films was unchanged by the addition of L. ruthenicum anthocyanins. Maciel et al.53 found the thermal degradation processes of chitosan–pectin films with and without anthocyanins were similar, indicating that the addition of anthocyanins did not affect the interactions between the polymers.
image file: c9ra06628d-f6.tif
Fig. 6 TGA (A) and DTG (B) curves of starch and starch–BBE films.

3.12. Antioxidant ability of starch–BBE films

The DPPH radical scavenging test was used to determinate the antioxidant ability of different films. As shown in Fig. 7, starch film had the lowest DPPH radical scavenging ability (only 7.97% at 5 mg mL−1). The weak antioxidant property of starch film was attributed to the abundant hydroxyl groups in the structure of starch and glycerol that could quench DPPH radical.20 The addition of BBE significantly increased the DPPH radical scavenging ability of the films (24.39–75.01% at 5 mg mL−1). Notably, the DPPH radical scavenging ability of the films increased with the increase of BBE content. The enhanced DPPH radical scavenging ability of the films was mainly attributed to the presence of anthocyanins that possessed potent antioxidant property. Due to abundant phenolic hydroxyl groups in the structures, anthocyanins could donate free electron or hydrogen atoms to reactive free radicals, thereby quenching free radicals.54 Similarly, other researchers also found the antioxidant property of starch-based films were greatly enhanced by the addition of anthocyanin-rich L. ruthenicum extract and blackberry berry pulp.20,45
image file: c9ra06628d-f7.tif
Fig. 7 DPPH radical scavenging activity of starch and starch–BBE films. Each value represents mean ± SD of triplicates.

3.13. pH-sensitive property of starch–BBE films

In order to evaluate the pH-sensitive property of the films, the representative starch–BBE I film was exposed to hydrogen chloride and ammonia gases, respectively (Fig. 8). The purple red color of the film gradually deepened in the hydrogen chloride gas, which was caused by the structure transformation of anthocyanins from quinonoidal anhydrobase (purple) into flavylium cation (red). Table S1 summarizes the color parameters of starch–BBE I film exposed to hydrogen chloride gas for different times. The gradually increased a values confirmed the film became red. When exposed to ammonia gas, the color of the film quickly turned blue in 5 min and then changes into olive color after 35 min, which was related with the structure transformation of anthocyanins from carbinol pseudobase to chalcone.38 Zhang et al.39 suggested that ammonia gas firstly diffused into the film matrix and then hydrolyzed to produce hydroxyl ions, which made an alkaline environment for the film. Table S2 summarizes the color parameters of starch–BBE I film exposed to ammonia gas for different times. The film exhibited negative b values before 35 min whereas presented positive b values thereafter. In addition, the b values of the film gradually increased with the extension of time. The changes in the color parameters were in good agreement with the observed color changes of the film. Above results indicated starch–BBE film was highly sensitive to pH changes. In other words, the film containing 1 wt% of BBE was sufficient to reflect the changes of environmental pH. Wu et al.34 found the chitosan/agarose film containing anthocyanins turned dark pink in less than 2 min in hydrogen chloride and turned purple after merely 2 min in ammonia gas, which was somewhat different from the results of our study. The differences in the color changes of the films could be due to the differences in the anthocyanin composition as well as the testing conditions (e.g. gas concentration and testing time). Our results suggested starch–BBE I film was pH-sensitive and could be used as a pH indicator to monitor the freshness of food products.
image file: c9ra06628d-f8.tif
Fig. 8 Color changes of starch–BBE I film after being exposed to hydrogen chloride and ammonia gases for different times.

3.14. Application of starch–BBE films for monitoring the freshness of pork

Fresh pork is highly susceptible to microbial contamination when exposed to the air, causing deterioration. Microbiological spoilage can produce a high level of TVB-N and change the pH value of pork.55 Since starch–BBE I film was pH-sensitive, it was further used to monitor the freshness of pork. As shown in Table 4, the initial TVB-N value of fresh pork was 8.35 mg/100 g. The TVB-N value of the pork increased to 10.35 mg/100 g when storage at 25 °C for 16 h. Notably, the TVB-N value of the pork reached 17.16 mg/100 g, which exceeded the limitation of Chinese Standard of GB 2707-2016 for edible pork (15 mg/100 g). This suggested that the pork had seriously deteriorated at this stage. Similar results were also reported by other researchers,20,56 who also found pork rotted at 25 °C in 24 h. With the extension of storage time to 48 h, the TVB-N value of pork even reached 34.28 mg/100 g. Meanwhile, starch–BBE I film showed significant color changes with the increase of the TVB-N value. Starch–BBE I film presented the purple/light color blue in the first 16 h and the orange color at 24–32 h and the yellow color thereafter. Table S3 summarizes the color parameters of starch–BBE I film at different storage times. The film showed negative b values before 24 h and positive b value afterwards. In addition, the b values of the film gradually increased with the extension of storage time. The changes in b values of the film were consistent with its color changes. Therefore, starch–BBE I film could be used to effectively reflect the freshness of pork during storage.
Table 4 The change of TVB-N levels in the pork as well as the color response of starch–BBE I film at different storage timesa
Time (h) TVB-N levels (mg/100 g) Color response of starch–BBE I film
a Values are given as mean ± SD (n = 3). Different letters in the same column indicate significantly different (p < 0.05).
0 8.35 ± 0.61f image file: c9ra06628d-u1.tif
8 8.77 ± 0.78f image file: c9ra06628d-u2.tif
16 10.35 ± 0.21e image file: c9ra06628d-u3.tif
24 17.16 ± 1.15d image file: c9ra06628d-u4.tif
32 22.10 ± 0.70c image file: c9ra06628d-u5.tif
40 28.01 ± 1.59b image file: c9ra06628d-u6.tif
48 34.28 ± 1.17a image file: c9ra06628d-u7.tif


4. Conclusion

Food packaging films with antioxidant and pH-sensitive properties were successfully developed by incorporating different contents of BBE into cassava starch. Notably, 1 wt% of BBE addition improved the water vapor barrier property and TS of the film, which was because the incorporation of a low content of BBE created a more dense and compact film network. Due to the presence of anthocyanins in BBE, starch–BBE films showed enhanced UV-vis light barrier, antioxidant and pH-sensitive properties. In future, starch–BBE films can be further used as intelligent films to monitor the freshness of different food products.

Conflicts of interest

There are no conflicts of interest to declare.

Acknowledgements

This work was supported by Grants-in-Aid for scientific research from the National Natural Science Foundation of China (No. 31571788), Innovation and Entrepreneurship Training Program for College Students in Jiangsu Province (No. 201811117061Y) and Northern Jiangsu Science and Technology Project (No. SZ-YC2018002).

References

  1. A. Valdés, A. C. Mellinas, M. Ramos, N. Burgos, A. Jiménez and M. D. C. Garrigós, RSC Adv., 2015, 5, 40324–40335 RSC.
  2. M. Kaya, S. Khadem, Y. S. Cakmak, M. Mujtaba, S. Ilk, L. Akyuz and E. Deligöz, RSC Adv., 2018, 8, 3941–3950 RSC.
  3. R. Thakur, P. Pristijono, C. J. Scarlett, M. Bowyer, S. P. Singh and Q. V. Vuong, Int. J. Biol. Macromol., 2019, 132, 1079–1089 CrossRef CAS.
  4. E. Basiak, A. Lenart and F. Debeaufort, Int. J. Biol. Macromol., 2017, 98, 348–356 CrossRef CAS.
  5. S. Santacruz, C. Rivadeneira and M. Castro, Food Hydrocolloids, 2015, 49, 89–94 CrossRef CAS.
  6. C. L. Luchese, V. F. Abdalla, J. C. Spada and I. C. Tessaro, Food Hydrocolloids, 2018, 82, 209–218 CrossRef CAS.
  7. T. Niranjana Prabhu and K. Prashantha, Polym. Compos., 2018, 39, 2499–2522 CrossRef CAS.
  8. B. Iamareerat, M. Singh, M. B. Sadiq and A. K. Anal, J. Food Sci. Technol., 2018, 55, 1953–1959 CrossRef CAS.
  9. J. H. R. Llanos and C. C. Tadini, Int. J. Biol. Macromol., 2018, 107, 371–382 CrossRef CAS.
  10. C. M. Jaramillo, T. J. Gutiérrez, S. Goyanes, C. Bernal and L. Famá, Carbohydr. Polym., 2016, 151, 150–159 CrossRef.
  11. S. Silva, E. M. Costa, C. Calhau, R. M. Morais and M. E. Pintado, Crit. Rev. Food Sci. Nutr., 2017, 57, 3072–3083 CrossRef CAS.
  12. V. O. Silva, A. A. Freitas, A. L. Maçanita and F. H. Quina, J. Phys. Org. Chem., 2016, 29, 594–599 CrossRef CAS.
  13. H. E. Khoo, A. Azlan, S. T. Tang and S. M. Lim, Food Nutr. Res., 2017, 61, 1361779 CrossRef.
  14. I. Choi, J. Y. Lee, M. Lacroix and J. Han, Food Chem., 2017, 218, 122–128 CrossRef CAS PubMed.
  15. V. A. Pereira Jr, I. N. Q. de Arruda and R. Stefani, Food Hydrocolloids, 2015, 43, 180–188 CrossRef.
  16. R. Andretta, C. L. Luchese, I. C. Tessaro and J. C. Spada, Food Hydrocolloids, 2019, 93, 317–324 CrossRef CAS.
  17. L. B. Golasz, J. da Silva and S. B. da Silva, Food Sci. Technol., 2013, 33, 155–162 CrossRef.
  18. C. L. Luchese, T. Garrido, J. C. Spada, I. C. Tessaro and K. de la Caba, Int. J. Biol. Macromol., 2018, 106, 834–839 CrossRef CAS.
  19. C. L. Luchese, J. Uranga, J. C. Spada, I. C. Tessaro and K. de la Caba, Int. J. Biol. Macromol., 2018, 115, 955–960 CrossRef CAS.
  20. Y. Qin, Y. Liu, H. Yong, J. Liu, X. Zhang and J. Liu, Int. J. Biol. Macromol., 2019, 134, 80–90 CrossRef CAS PubMed.
  21. P. Veiga-Santos, C. Ditchfield and C. C. Tadini, J. Appl. Polym. Sci., 2011, 120, 1069–1079 CrossRef CAS.
  22. S. Zhou, Z. Fang, Y. Lü, J. Chen, D. Liu and X. Ye, Food Chem., 2009, 112, 394–399 CrossRef CAS.
  23. C. Sun, H. Huang, C. Xu, X. Li and K. Chen, Plant Foods Hum. Nutr., 2013, 68, 97–106 CrossRef CAS PubMed.
  24. Z. Fang, Y. Zhang, Y. Lü, G. Ma, J. Chen, D. Liu and X. Ye, Food Chem., 2009, 113, 884–888 CrossRef CAS.
  25. J. Bao, Y. Cai, M. Sun, G. Wang and H. Corke, J. Agric. Food Chem., 2005, 53, 2327–2332 CrossRef CAS.
  26. Z. Fang, M. Zhang and L. Wang, Food Chem., 2007, 100, 845–852 CrossRef CAS.
  27. B. Zhang, M. Kang, Q. Xie, B. Xu, C. Sun, K. Chen and Y. Wu, J. Agric. Food Chem., 2010, 59, 537–545 CrossRef.
  28. W. Duan, S. Jin, G. Zhao and P. Sun, Food Sci. Technol., 2015, 35, 524–530 CrossRef.
  29. J. Ge, P. Yue, J. Chi, J. Liang and X. Gao, Food Hydrocolloids, 2018, 74, 23–31 CrossRef CAS.
  30. X. Zhang, Y. Liu, H. Yong, Y. Qin, J. Liu and J. Liu, Food Hydrocolloids, 2019, 94, 80–92 CrossRef CAS.
  31. L. Stoll, T. M. H. Costa, A. Jablonski, S. H. Flôres and A. de Oliveira Rios, Food Bioprocess Technol., 2016, 9, 172–181 CrossRef CAS.
  32. X. Wang, H. Yong, L. Gao, L. Li, M. Jin and J. Liu, Food Hydrocolloids, 2019, 89, 56–66 CrossRef CAS.
  33. J. Liu, C. Meng, S. Liu, J. Kan and C. Jin, Food Hydrocolloids, 2017, 63, 457–466 CrossRef CAS.
  34. S. Wu, W. Wang, K. Yan, F. Ding, X. Shi, H. Deng and Y. Du, Carbohydr. Polym., 2018, 186, 236–242 CrossRef CAS.
  35. Z. Zhang, J. Li and L. Fan, Food Chem., 2019, 276, 451–457 CrossRef CAS.
  36. X. Zhang, H. Huang, Q. Zhang, F. Fan, C. Xu, C. Sun, X. Li and K. Chen, Int. J. Mol. Sci., 2015, 16, 12467–12481 CrossRef CAS.
  37. Q. Ma, T. Liang, L. Cao and L. Wang, Int. J. Biol. Macromol., 2018, 108, 576–584 CrossRef CAS.
  38. K. Halász and L. Csóka, Food Packaging and Shelf Life, 2018, 16, 185–193 CrossRef.
  39. J. Zhang, X. Zou, X. Zhai, X. Huang, C. Jiang and M. Holmes, Food Chem., 2019, 272, 306–312 CrossRef CAS.
  40. H. Yong, X. Wang, R. Bai, Z. Miao, X. Zhang and J. Liu, Food Hydrocolloids, 2019, 90, 216–224 CrossRef CAS.
  41. J. Liu, X. Wang, F. Wen, S. Zhang, R. Shen, W. Jiang, J. Kan and C. Jin, Int. J. Biol. Macromol., 2016, 93, 107–116 CrossRef CAS PubMed.
  42. T. J. Gutiérrez, L. A. Toro-Márquez, D. Merino and J. R. Mendieta, Food Hydrocolloids, 2019, 89, 283–293 CrossRef.
  43. X. Zhai, J. Shi, X. Zou, S. Wang, C. Jiang, J. Zhang, X. Huang, W. Zhang and M. Holmes, Food Hydrocolloids, 2017, 69, 308–317 CrossRef CAS.
  44. M. Kurek, I. E. Garofulić, M. T. Bakić, M. Ščetar, V. D. Uzelac and K. Galić, Food Hydrocolloids, 2018, 84, 238–246 CrossRef CAS.
  45. G. F. Nogueira, C. T. Soares, R. Cavasini, F. M. Fakhouri and R. A. de Oliveira, Food Chem., 2019, 275, 417–425 CrossRef CAS.
  46. C. G. Vargas, T. M. H. Costa, A. de Oliveira Rios and S. H. Flôres, Food Hydrocolloids, 2017, 65, 96–106 CrossRef CAS.
  47. L. A. Toro-Márquez, D. Merino and T. J. Gutiérrez, Food Bioprocess Technol., 2018, 11, 1955–1973 CrossRef.
  48. J. Peralta, C. M. Bitencourt-Cervi, V. B. Maciel, C. M. Yoshida and R. A. Carvalho, Food Packaging and Shelf Life, 2018, 19, 47–55 CrossRef.
  49. A. Ashrafi, M. Jokar and A. M. Nafchi, Int. J. Biol. Macromol., 2018, 108, 444–454 CrossRef CAS.
  50. T. J. Gutiérrez and V. A. Alvarez, Food Hydrocolloids, 2018, 77, 407–420 CrossRef.
  51. M. Koosha and S. Hamedi, Prog. Org. Coat., 2019, 127, 338–347 CrossRef CAS.
  52. T. J. Gutiérrez, J. Suniaga, A. Monsalve and N. L. García, Food Hydrocolloids, 2016, 54, 234–244 CrossRef.
  53. V. B. V. Maciel, C. M. P. Yoshida and T. T. Franco, Carbohydr. Polym., 2015, 132, 537–545 CrossRef CAS.
  54. A. Castaneda-Ovando, M. de Lourdes Pacheco-Hernández, M. E. Páez-Hernández, J. A. Rodríguez and C. A. Galán-Vidal, Food Chem., 2009, 113, 859–871 CrossRef CAS.
  55. J. Liu, H. Wang, P. Wang, M. Guo, S. Jiang, X. Li and S. Jiang, Food Hydrocolloids, 2018, 83, 34–142 CrossRef.
  56. H. Yong, J. Liu, Y. Qin, R. Bai, X. Zhang and J. Liu, Int. J. Biol. Macromol., 2019, 137, 307–316 CrossRef CAS PubMed.

Footnotes

Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ra06628d
These authors contributed equally to this work.