Epitaxially grown single-crystalline SrTiO3 membranes using a solution-processed, amorphous SrCa2Al2O6 sacrificial layer

Abstract

Water-soluble sacrificial layers based on epitaxially grown, single crystalline (Ca, Sr, Ba)3Al2O6 layers are widely used for creating free-standing perovskite oxide membranes. However, obtaining these sacrificial layers with intricate stoichiometry remains a challenge, especially for molecular beam epitaxy (MBE). In this study, we demonstrate the hybrid MBE growth of epitaxial, single crystalline SrTiO3 films using a solution processed, amorphous SrCa2Al2O6 sacrificial layer onto SrTiO3 (001) substrates. Prior to the growth, oxygen plasma exposure was used to first create the crystalline SrCa2Al2O6 layer with well-defined surface crystallinity. Utilizing reflection high energy electron diffraction, X-ray diffraction, and atomic force microscopy, we observe an atomic layer-by-layer growth of epitaxial, single crystalline SrTiO3 films on the SrCa2Al2O6 layer with atomically smooth surfaces. The SrCa2Al2O6 layer was subsequently dissolved in deionized water to create free-standing SrTiO3 membranes that were transferred onto a metal-coated Si wafer. Membranes created with Sr-deficiency revealed ferroelectric-like behavior measured using piezo-force microscopy whereas stoichiometric films retained paraelectric-like behavior. These findings underscore the viability of using ex situ deposited amorphous SrCa2Al2O6 for epitaxial, single crystalline growth, as well as the importance of point defects in determining the ferroic properties in membranes.

Graphical abstract: Epitaxially grown single-crystalline SrTiO3 membranes using a solution-processed, amorphous SrCa2Al2O6 sacrificial layer

Supplementary files

Article information

Article type
Communication
Submitted
16 মে 2024
Accepted
16 আগ. 2024
First published
16 আগ. 2024

J. Mater. Chem. C, 2024,12, 13809-13815

Epitaxially grown single-crystalline SrTiO3 membranes using a solution-processed, amorphous SrCa2Al2O6 sacrificial layer

S. Varshney, M. Ramis, S. Choo, M. Coll and B. Jalan, J. Mater. Chem. C, 2024, 12, 13809 DOI: 10.1039/D4TC02030H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements