Defect induced photoluminescence and triboluminescence in layered CaLaAl3O7

Abstract

In this work, a layered melilite structure, CaLaAl3O7, was synthesized and observed to have obvious luminescence behaviors under the stimuli of ultraviolet light and rubbing, which were called photoluminescence and triboluminescence, respectively. Considering the wide bandgap of CaLaAl3O7 and its specific crystal structure, the observed luminescence should be attributed to intrinsic defects. Both the photoluminescence and triboluminescence of CaLaAl3O7 show a strong dependence on the synthesis atmosphere, suggesting that they should be related to the oxygen vacancy. It is attractive to find that the triboluminescence of CaLaAl3O7 shows a distinct spectral characteristic compared to its photoluminescence. Further computational results suggest that the applied mechanical stimuli on the CaLaAl3O7 cell could promote the formation of the vacancies of oxygen and calcium, responsible for the spectral differences.

Graphical abstract: Defect induced photoluminescence and triboluminescence in layered CaLaAl3O7

Supplementary files

Article information

Article type
Communication
Submitted
29 сеп 2019
Accepted
03 ное 2019
First published
04 ное 2019

Dalton Trans., 2020,49, 3942-3945

Defect induced photoluminescence and triboluminescence in layered CaLaAl3O7

Y. Li, I. P. Koskin, Z. Ma, E. Benassi and Z. Wang, Dalton Trans., 2020, 49, 3942 DOI: 10.1039/C9DT03849C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements