Design of a novel scandium silicate based blue-emitting phosphor with high efficiency and robust thermal stability for warm WLEDs and field emission displays

Abstract

A novel blue-emitting phosphor, Na3ScSi2O7:Ce3+ (NSSO:Ce3+), was synthesized with a solid-state method at low temperature successfully. Its crystal structure, band structure, and photoluminescence and cathodoluminescence properties were researched in detail. The phase formation and the crystal structure were confirmed by powder X-ray diffraction analysis and the Rietveld refinement method, respectively. Under the excitation of n-UV light, the optimal NSSO:0.02Ce3+ phosphor can yield blue emission centered at 452 nm with a high quantum efficiency of 50.9%. The PL intensity of the NSSO:0.02Ce3+ phosphor remains at 71.46% of the initial value when the temperature is increased from room temperature to 150 °C, indicating good thermal stability. A WLED lamp was obtained by combining a 360 nm n-UV chip with Sr2SiO4:Eu2+, (Ca, Sr)AlSiN3:Eu2+ and NSSO:0.02Ce3+ phosphors, in which the color coordinates, CCT and CRI are (0.360, 0.348), 4409 K and 90.9, respectively. Moreover, under low voltage electron bombardment, the phosphor can emit blue emission with high luminescence intensity, current saturation and resistance. All the results indicate that the NSSO:Ce3+ phosphor shows much potential for the application of both WLEDs and field emission displays (FEDs). Our research has also offered a new insight and perspective that using Sc-based sorosilicates as host can be an appropriate  strategy for developing excellent inorganic luminescence materials.

Graphical abstract: Design of a novel scandium silicate based blue-emitting phosphor with high efficiency and robust thermal stability for warm WLEDs and field emission displays

Article information

Article type
Research Article
Submitted
07 юни 2019
Accepted
13 авг 2019
First published
14 авг 2019

Mater. Chem. Front., 2019,3, 2120-2127

Design of a novel scandium silicate based blue-emitting phosphor with high efficiency and robust thermal stability for warm WLEDs and field emission displays

Q. Zhang, X. Wang, Z. Tang and Y. Wang, Mater. Chem. Front., 2019, 3, 2120 DOI: 10.1039/C9QM00370C

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements