Thermal evolution of structures and conductivity of Pr-substituted BaZr0.7Ce0.2Y0.1O3−δ: potential cathode components for protonic ceramic fuel cells

Abstract

A complete solid solution forms between the perovskite proton conductor BaZr0.7Ce0.2Y0.1O3−δ (BZCY72) and BaPr0.9Y0.1O3−δ (BPY) on synthesis by the Pechini method and high-temperature annealing. Phase fields of selected members of the Ba(Zr0.7Ce0.2)1−(x/0.9)PrxY0.1O3−δ series were studied as a function of composition and temperature by high-resolution neutron powder diffraction revealing symmetry changes in the sequence PnmaImmaImage ID:c7ta09570h-t1.gifPm[3 with combining macron]m. Higher symmetry is favoured for low Pr contents and high temperatures, as consideration of tolerance factor suggests. A volume contraction, ascribed to dehydration, is observed by synchrotron X-ray diffraction on heating in air for lower x. Magnetic measurements and structural data support the presence of Pr in the IV valence state on the perovskite B site. Thermogravimetric analysis in CO2 to ∼1253 K indicates better chemical stability for x ≤ 0.445, whereas decomposition occurred for higher x. Electrical conductivity increases by over two orders of magnitude in dry air at lower temperature from x = 0.225 to 0.675; total conductivity reaches a value of 0.4 S cm−1 at 1173 K for x = 0.675. The series exhibits electron–hole transport with a positive pO2 dependence which increases with temperature, consistent with participation of oxygen vacancies in charge compensation of the Y3+ acceptor dopant. The activation energy for thermally activated hole hopping in air in the range 523–773 K decreases from ∼1 eV for BZCY72 to ∼0.4 eV for x = 0.675. Conductivity is generally lower in humidified N2 and air (pH2O ≈ 0.023 atm) than the corresponding dry atmospheres, consistent with consumption of holes by less mobile protonic species; however for x ≤ 0.225 the lower concentration of electron holes concomitant with higher oxygen-vacancy content in N2 results in slightly higher conductivity in wet conditions due to hydration of vacancies.

Graphical abstract: Thermal evolution of structures and conductivity of Pr-substituted BaZr0.7Ce0.2Y0.1O3−δ: potential cathode components for protonic ceramic fuel cells

Article information

Article type
Paper
Submitted
30 окт 2017
Accepted
20 ное 2017
First published
20 ное 2017

J. Mater. Chem. A, 2018,6, 5324-5334

Thermal evolution of structures and conductivity of Pr-substituted BaZr0.7Ce0.2Y0.1O3−δ: potential cathode components for protonic ceramic fuel cells

G. Heras-Juaristi, U. Amador, R. O. Fuentes, A. L. Chinelatto, J. Romero de Paz, C. Ritter, D. P. Fagg, D. Pérez-Coll and G. C. Mather, J. Mater. Chem. A, 2018, 6, 5324 DOI: 10.1039/C7TA09570H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements