Adsorption-controlled growth and the influence of stoichiometry on electronic transport in hybrid molecular beam epitaxy-grown BaSnO3 films

Abstract

High room-temperature electron mobility and optical transparency in the visible spectrum distinguishes BaSnO3 from other perovskite oxides. The origin of low mobility in thin films as compared to their bulk counterpart is attributed to the presence of dislocations in films with nearly no discussion on the role of point defects such as cation non-stoichiometry. Using high-resolution X-ray diffraction, Rutherford backscattering spectrometry, thermal, and electronic transport measurements, we show that a growth window, in which cation stoichiometry is self-regulating, can be achieved for BaSnO3 films on SrTiO3(001) and (La0.3Sr0.7)(Al0.65Ta0.35)O3(001) (LSAT) substrates using a hybrid molecular beam epitaxy approach. BaSnO3 films on SrTiO3 grown within the growth window yielded a mobility value of 105 cm2 V−1 s−1 at a density, 2.5 × 1020 cm−3. Bulk-like thermal conductivity of 13.3 ± 1.46 W m−1 K−1 was achieved for stoichiometric films. Both Ba- and Sn-deficient films resulted into charge compensation and low mobility, with a stronger dependence for Sn-deficient films.

Graphical abstract: Adsorption-controlled growth and the influence of stoichiometry on electronic transport in hybrid molecular beam epitaxy-grown BaSnO3 films

Supplementary files

Article information

Article type
Paper
Submitted
12 яну 2017
Accepted
07 фев 2017
First published
08 фев 2017

J. Mater. Chem. C, 2017,5, 5730-5736

Adsorption-controlled growth and the influence of stoichiometry on electronic transport in hybrid molecular beam epitaxy-grown BaSnO3 films

A. Prakash, P. Xu, X. Wu, G. Haugstad, X. Wang and B. Jalan, J. Mater. Chem. C, 2017, 5, 5730 DOI: 10.1039/C7TC00190H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements