Issue 69, 2014

Vacuum-annealing-tailored robust and flexible nanopore-structured γ-Fe2O3 film anodes for high capacity and long life Na-ion batteries

Abstract

Relatively high cost and limited resources are limiting the broad applications of Li-ion batteries. Na-ion batteries are one of the most promising replacement candidates because of abundant sodium resources, low price and similarity with Li insertion chemistry. For the first time, γ-Fe2O3 film was grown directly on a copper sheet with radio frequency magnetron sputtering as an anode for Na-ion batteries. Results show that the γ-Fe2O3 film annealed at 600 °C delivers a high reversible capacity of 450 mA h g−1 and nearly 100% capacity retention over 100 charge–discharge cycles, significantly outperforming all the previously reported examples. It is believed that the high performance of the Na-ion anode can be attributed to high temperature annealing producing nanopores for a large ion-inserting surface area and uniform γ-Fe2O3 particles firmly loaded on the surface of the Cu substrate to robustly retain the film structure during the Na-ion intercalation process for long cycle life. This work holds great promise for the fabrication of inexpensive and non-toxic Na-ion batteries for practical applications.

Graphical abstract: Vacuum-annealing-tailored robust and flexible nanopore-structured γ-Fe2O3 film anodes for high capacity and long life Na-ion batteries

Article information

Article type
Paper
Submitted
19 май 2014
Accepted
31 юли 2014
First published
01 авг 2014

RSC Adv., 2014,4, 36815-36820

Vacuum-annealing-tailored robust and flexible nanopore-structured γ-Fe2O3 film anodes for high capacity and long life Na-ion batteries

B. Sun, S. J. Bao, J. Le Xie and C. M. Li, RSC Adv., 2014, 4, 36815 DOI: 10.1039/C4RA04686B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements