Electrolyte tuning with low concentrations of additive for dendrite suppression in lithium metal anodes

Abstract

Lithium (Li) metal is considered to be an ideal anode for high-energy density storage systems. However, its high reactivity and instability towards organic electrolytes leads to continuous consumption of electrolytes and Li metal, causing dendrite growth. This induces safety issues and low cyclability, which hinders its practical use. Although electrolyte additives are extensively utilized to address these issues, the practice remains challenging due to the least understanding of their interactions with electrolytic environments. Here, we report a novel electrolyte additive, gadolinium nitrate (Gd(NO3)3), with a low optimal concentration of 3 mM in a lithium bis(trifluoromethanesulfonyl)imide-lithium nitrate (LiTFSI-LiNO3) ether-based electrolyte; this additive promotes plating/stripping of Li in nodular morphology, significantly suppressing dendrites and dead Li growth while improving the cycle life and overall stability of Li metal batteries. A significant reduction is observed in the Li-metal electrode overpotential under a current density of 2 mA cm−2. When a Li metal battery was tested with LiFePO4 (LFP) cathode at an active mass loading of 4 mg cm−2, a capacity retention of 98.33% was observed after 400 cycles. Such stable cycling and enhanced performance are attributed to the formation of a chemically stable, mechanically robust, and ionically conductive solid electrolyte interphase (SEI) layer on the Li metal surface, which is enabled by the incorporation of Gd(NO3)3 compared to cells with pristine Li electrolytes.

Graphical abstract: Electrolyte tuning with low concentrations of additive for dendrite suppression in lithium metal anodes

Supplementary files

Article information

Article type
Communication
Submitted
25 apr 2024
Accepted
04 iyl 2024
First published
04 iyl 2024
This article is Open Access
Creative Commons BY-NC license

Sustainable Energy Fuels, 2024,8, 3574-3582

Electrolyte tuning with low concentrations of additive for dendrite suppression in lithium metal anodes

A. Baniya, M. B. Saud, H. Li, M. B. Faheem, Y. Zhang, A. Thapa, R. S. Bobba, P. I. Kaswekar and Q. Qiao, Sustainable Energy Fuels, 2024, 8, 3574 DOI: 10.1039/D4SE00548A

This article is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported Licence. You can use material from this article in other publications, without requesting further permission from the RSC, provided that the correct acknowledgement is given and it is not used for commercial purposes.

To request permission to reproduce material from this article in a commercial publication, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party commercial publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements